Evaluation of WC-17Co and WC-10Co-4Cr thermal spray coatings by HVOF on the fatigue and corrosion strength of AISI 4340 steel
(Elsevier B.V., 2005-01-21)
It is known that chromium electroplating is related to the reduction in the fatigue strength of base metal. However, chromium results in protection against wear and corrosion combined with chemical resistance and good ...
Fatigue Performance of AISI 4340 Steel Ni-Cr-B-Si-Fe HVOF Thermal Spray Coated
(2015-01-01)
Coatings are deposited on high strength materials to improve the surface degradation resistance of several elements. As a consequence, the fatigue strength of coated materials is significantly influenced by internal residual ...
Evaluation of WC-10Ni thermal spray coating with shot peening on the fatigue strength of AISI 4340 steel
(Elsevier B.V., 2010-01-01)
Fatigue failure is a result of a crack initiation and propagation, in consequence of a cyclical load. In aeronautical components as landing gear the fatigue strength is an important parameter to be considered in project, ...
Evaluation of WC-10Ni thermal spray coating with shot peening on the fatigue strength of AISI 4340 steel
(Elsevier B.V., 2010-01-01)
Fatigue failure is a result of a crack initiation and propagation, in consequence of a cyclical load. In aeronautical components as landing gear the fatigue strength is an important parameter to be considered in project, ...
Effect of Alloying Elements on Thermal Diffusivity of Gray Cast Iron Used in Automotive Brake Disks
(SPRINGER, 2009)
The purpose of this work was to experimentally investigate the thermal diffusivity of four different gray cast iron alloys, regularly used to produce brake disks for automotive vehicles. Thermal diffusivity measurements ...
Fatigue strength of HVOF sprayed Cr(3)C(2)-25NiCr and WC-10Ni on AISI 4340 steel
(Elsevier B.V. Sa, 2008-11-25)
The fatigue strength of coated material is significantly influenced by internal residual stresses. Chromium coatings are used in applications to guarantee protection against wear and corrosion, combined with chemical ...
EVALUATION OF HVOF SPRAYED WC-13Co-4Cr AND HARD CHROMIUM ELECTROPLATED ON STAINLESS STEEL 15-5PH FATIGUE STRENGTH
(Inegi-feup, 2017-01-01)
Fatigue failure is the result of a crack initiation and propagation as a consequence of cyclic loading. In the aeronautical industry, for components like landing gear, fatigue strength is an important parameter to be ...
Evaluation of WC-17Co and WC-10Co-4Cr thermal spray coatings by HVOF on the fatigue and corrosion strength of AISI 4340 steel
(Elsevier B.V., 2005-01-21)
It is known that chromium electroplating is related to the reduction in the fatigue strength of base metal. However, chromium results in protection against wear and corrosion combined with chemical resistance and good ...