Influence of the degradation on the stress cracking values of high density polyethylene (HDPE) geomembranes after different exposures

Universidade de São Paulo (USP); Universidade Estadual Paulista (Unesp) (2012-12-03)

This paper presents results from stress cracking (SC) tests performed in both fresh and exposed high density polyethylene (HDPE) geomembranes (GM). The HDPE GMs were exposed to ultraviolet radiation, thermal aging (air ...

Influence of the degradation on the stress cracking values of high density polyethylene (HDPE) geomembranes after different exposures

Universidade de São Paulo (USP); Universidade Estadual Paulista (Unesp) (2012-12-03)

Effect of thermal treatments on tensile strength of commercially cast pure titanium and Ti-6Al-4V alloys

Universidade Estadual Paulista (Unesp); Universidade Estadual de Campinas (UNICAMP) (2005-08-01)

Heating titanium structures is assumed to relieve tensions induced by the casting process as well as possibly optimizing some mechanical properties. The aim of this investigation was to evaluate the effect of thermal ...

Effect of thermal treatments on tensile strength of commercially cast pure titanium and Ti-6Al-4V alloys

Universidade Estadual Paulista (Unesp); Universidade Estadual de Campinas (UNICAMP) (2005-08-01)

Influence of the degradation on the stress cracking values of high density polyethylene (HDPE) geomembranes after different exposures

Lavoie, Fernando Luiz; Bueno, Benedito de Souza; Lodi, Paulo César (2014)

Determining the tensile stress-crack opening curve of concrete by inverse analysis

de Oliveira, JLA; Gettu, R (Asce-amer Soc Civil EngineersRestonEUA, 2006)

Apparatus to perform creep tests under constant tensile stress

FERREIRA, I.; 32rd REUNIAO ANUAL DA SOCIEDADE BRASILEIRA PARA O PROGRESSO DA CIENCIA (2014)

Effect of thermal treatments on tensile strength of commercially cast pure titanium and Ti-6Al-4V alloys

Rocha, Sicknan Soares da; Adabo, Gelson Luis; Vaz, Luis Geraldo; Henriques, Guilherme Elias Pessanha (2014)

Whole-field analysis of uniaxial tensile tests by Moire interferometry

Cordero, RR; Francois, M; Lira, I; Vial Edwards, C (ELSEVIER SCI LTD, 2005)

Moire interferometry-a high sensitivity whole-field optical technique-was used to follow the evolution of the deformation process of an aluminium sample subjected to a uniaxial tensile test. This technique allowed us to ...

The effect of mass scaling and speed increase in explicit dynamic simulations using tensile test

PEREIRA, L.S.; DONATO, G.H.B.; MATTAR NETO, MIGUEL; INTERNATIONAL NUCLEAR ATLANTIC CONFERENCE (Associa????o Brasileira de Energia Nuclear, 2021)

1
2
3
4
. . .
182

Buscar

Filtros

Influence of the degradation on the stress cracking values of high density polyethylene (HDPE) geomembranes after different exposures

Influence of the degradation on the stress cracking values of high density polyethylene (HDPE) geomembranes after different exposures

Effect of thermal treatments on tensile strength of commercially cast pure titanium and Ti-6Al-4V alloys

Effect of thermal treatments on tensile strength of commercially cast pure titanium and Ti-6Al-4V alloys

Influence of the degradation on the stress cracking values of high density polyethylene (HDPE) geomembranes after different exposures

Determining the tensile stress-crack opening curve of concrete by inverse analysis

Apparatus to perform creep tests under constant tensile stress

Effect of thermal treatments on tensile strength of commercially cast pure titanium and Ti-6Al-4V alloys

Whole-field analysis of uniaxial tensile tests by Moire interferometry

The effect of mass scaling and speed increase in explicit dynamic simulations using tensile test