CdMoO 4 synthesized by a microwave-assisted hydrothermal method and their photoluminescence and photocatality properties
(2012-08-20)
In this work CdMoO 4 nanoparticles were obtained under hydrothermal conditions using microwave radiation (2.45 GHz) (MH) at 100°C for different times. These powders were analyzed by X-ray diffraction (XRD), Field-emisson ...
Preparation and photoluminescence characteristics of In(OH) 3:xTb3+ obtained by Microwave-Assisted Hydrothermal method
(2013-03-15)
Crystalline terbium-doped indium hydroxide structures were prepared by a rapid and efficient Microwave-Assisted Hydrothermal (MAH) method. Nanostructures were obtained at a low temperature. FE-SEM images confirm that these ...
Preparation and photoluminescence characteristics of In(OH) 3:xTb3+ obtained by Microwave-Assisted Hydrothermal method
(2013-03-15)
Crystalline terbium-doped indium hydroxide structures were prepared by a rapid and efficient Microwave-Assisted Hydrothermal (MAH) method. Nanostructures were obtained at a low temperature. FE-SEM images confirm that these ...
Intense photoluminescence emission at room temperature in calcium copper titanate powders
(2013-05-01)
A study was undertaken about the structural and photoluminescent properties at room temperature of CaCu3Ti4O12 (CCTO) powders synthesized by a soft chemical method and heat treated between 300 and 800 °C. The decomposition ...
Intense photoluminescence emission at room temperature in calcium copper titanate powders
(2013-05-01)
A study was undertaken about the structural and photoluminescent properties at room temperature of CaCu3Ti4O12 (CCTO) powders synthesized by a soft chemical method and heat treated between 300 and 800 °C. The decomposition ...
Influence of microwave energy on structural and photoluminescent behavior of CaTiO3 powders
(Elsevier B.V., 2008-08-01)
Calcium titanate, CaTiO3 powders were prepared by the polymeric precursor method and annealed at different temperatures for 2 h in a conventional furnace and for 30 min on an adapted microwave oven. The effect of microwave ...
Influence of microwave energy on structural and photoluminescent behavior of CaTiO3 powders
(Elsevier B.V., 2008-08-01)
Calcium titanate, CaTiO3 powders were prepared by the polymeric precursor method and annealed at different temperatures for 2 h in a conventional furnace and for 30 min on an adapted microwave oven. The effect of microwave ...
Enhancement of symmetry-induced photoluminescence in bismuth tungstate microcrystals
(2016-12-01)
Bi2WO6 (BWO) powders synthesized via hydrothermal processes were studied in order to determine the effect of structure on photoluminescence (PL). BWO samples were characterized using X-Ray Powder Diffraction, UV–vis diffuse ...