Preparation and photoluminescence characteristics of In(OH) 3:xTb3+ obtained by Microwave-Assisted Hydrothermal method
(2013-03-15)
Crystalline terbium-doped indium hydroxide structures were prepared by a rapid and efficient Microwave-Assisted Hydrothermal (MAH) method. Nanostructures were obtained at a low temperature. FE-SEM images confirm that these ...
Preparation and photoluminescence characteristics of In(OH) 3:xTb3+ obtained by Microwave-Assisted Hydrothermal method
(2013-03-15)
Crystalline terbium-doped indium hydroxide structures were prepared by a rapid and efficient Microwave-Assisted Hydrothermal (MAH) method. Nanostructures were obtained at a low temperature. FE-SEM images confirm that these ...
Intense photoluminescence emission at room temperature in calcium copper titanate powders
(2013-05-01)
A study was undertaken about the structural and photoluminescent properties at room temperature of CaCu3Ti4O12 (CCTO) powders synthesized by a soft chemical method and heat treated between 300 and 800 °C. The decomposition ...
Intense photoluminescence emission at room temperature in calcium copper titanate powders
(2013-05-01)
A study was undertaken about the structural and photoluminescent properties at room temperature of CaCu3Ti4O12 (CCTO) powders synthesized by a soft chemical method and heat treated between 300 and 800 °C. The decomposition ...
CdMoO 4 synthesized by a microwave-assisted hydrothermal method and their photoluminescence and photocatality properties
(2012-08-20)
In this work CdMoO 4 nanoparticles were obtained under hydrothermal conditions using microwave radiation (2.45 GHz) (MH) at 100°C for different times. These powders were analyzed by X-ray diffraction (XRD), Field-emisson ...
Spherical-shaped Y2O3:Eu3+ nanoparticles with intense photoluminescence emission
(Elsevier B.V., 2015-01-01)
Herein we report on the crystallized nanoparticles based on Eu3+-doped Y2O3 with 5 mol% using citric acid as precursor. The heating temperatures were evaluated in order to obtain the best crystallized nanoparticles with ...
Connecting morphology and photoluminescence emissions in β-Ag2MoO4 microcrystals
(2022-02-01)
This work elucidates the morphology-photoluminescence (PL) emission relationships, based on experimental and calculated results, on β-Ag2MoO4 samples synthesized by microwave-assisted hydrothermal method. It was shown that ...