On the creep behavior of carbon/epoxy non-crimp fabric composites
(2018-01-01)
The use of composites in structural applications requires the study of specific properties to ensure that these materials are safe and an excellent option to replace some metals, for example. In the present study, vacuum ...
Resistência de laminados com furo aberto considerando incertezas nas propriedades admissíveis do material
(Universidade Federal de Minas GeraisBrasilENG - DEPARTAMENTO DE ENGENHARIA ESTRUTURASPrograma de Pós-Graduação em Engenharia de EstruturasUFMG, 2015-09-25)
Laminates NCF (non-crimp fabrics) are the union of unidirectional layers through stitching threads. Those laminates gained visibility for structural applications due to its superior post-impact properties, greater speed ...
Influence of voids on the flexural resistance of the NCF/RTM6 composites
(Elsevier B.V., 2011-01-01)
A major difficulty to achieve maximum weight savings in the manufacture of composite structural components, is the tendency of these materials have the formation of voids and cracks in the interior and surface components. ...
Aplicación de criterio de falla para compuestos reforzados con Non-Crimp Fabrics en compuestos reforzados con tejido de fibra unidireccional.
(Universidad de Concepción.Departamento de Ingeniería MecánicaDepartamento de Ingeniería Mecánica., 2019)
Los materiales compuestos de polímero reforzado con fibra están siendo utilizados cada vez más
en una gran variedad de aplicaciones, dentro de las configuraciones estándares de refuerzos de
fibras, los tejidos unidireccionales ...
Influence of voids on the flexural resistance of the NCF/RTM6 composites
(Elsevier B.V., 2011-01-01)
A major difficulty to achieve maximum weight savings in the manufacture of composite structural components, is the tendency of these materials have the formation of voids and cracks in the interior and surface components. ...
Flexão e análise dinâmico-mecânica de compósitos 5HS e NCF com resina epóxi monocomponente produzidos por RTM
(Universidade Estadual Paulista (UNESP), 2015)
Flexão e análise dinâmico-mecânica de compósitos 5HS e NCF com resina epóxi monocomponente produzidos por RTM
(Universidade Estadual Paulista (Unesp), 2015)
Flexão e análise dinâmico-mecânica de compósitos 5HS e NCF com resina epóxi monocomponente produzidos por RTM
(Universidade Estadual Paulista (Unesp), 2012-08-25)
In order to study resin distribution and homogeneity of composite laminates manufactured by RTM, it was used CYCOM 890 monolithic toughened epoxy as a matrix with two different configurations of intermediated modulus (IM) ...
Influence of voids on the flexural resistance of the NCF/RTM6 composites
(Elsevier B.V., 2014)
Compósitos processados via RTM em molde de aço carbono e de liga de alumínio: efeito da condutividade térmica nas propriedades mecânicas e térmicas
(Universidade Estadual Paulista (Unesp), 2017-02-06)
O aumento do uso de compósitos estruturais tem levado a uma preocupação constante com a confiabilidade destes materiais. Em particular, o processo de cura das resinas na fabricação é citado como um dos problemas mais ...