Bond strength and monomer conversion of bonding agents mixed with restorative composites prior to light exposure
(Taylor & Francis LtdAbingdonInglaterra, 2007)
A new acrylated monomer from macaw vegetable oil that polymerizes without external photoinitiators
(2021-11-01)
The photopolymerization process has been widely studied due to its use in painting/coating, dentistry, creating photoresist materials and more recently in 3D printing. Therefore, new monomers have been synthesized to be ...
Monomer conversion of pre-heated composite
(Int Amer Assoc Dental Researchi A D R/a A D RAlexandriaEUA, 2005)
Theoretical prediction and experimental determination of the effect of mold characteristics on temperature and monomer conversion fraction profiles during polymerization of a PMMA-based bone cement
(Wiley, 2002-12)
The present work is concerned with applications of a kinetic model for free-radical polymerization of a polymethylmethacrylate-based bone cement. Autocatalytic behavior at the first part of the reaction as well as a diffusion ...
Effect of pre-heating resin composite and light-curing units on monomer conversion
(2010-01-01)
The purpose of this study was to evaluate the effect of pre-heating resin composite photo-cured with light-curing units (LCU) by FT-IR. Twenty specimens were made in a metallic mold (4 mm diameter × 2 mm thick) from composite ...
Effect of pre-heating resin composite and light-curing units on monomer conversion
(2010-01-01)
The purpose of this study was to evaluate the effect of pre-heating resin composite photo-cured with light-curing units (LCU) by FT-IR. Twenty specimens were made in a metallic mold (4 mm diameter × 2 mm thick) from composite ...
Effect of water-bath post-polymerization on the mechanical properties, degree of conversion, and leaching of residual compounds of hard chairside reline resins
(Elsevier B.V., 2009-05-01)
Objectives. This study evaluated the effect of water-bath post-polymerization at 55 degrees C for 10 min (WB) on the content and leaching of residual compounds, degree of conversion, flexural strength, and hardness of hard ...
Effect of water-bath post-polymerization on the mechanical properties, degree of conversion, and leaching of residual compounds of hard chairside reline resins
(Elsevier B.V., 2009-05-01)
Objectives. This study evaluated the effect of water-bath post-polymerization at 55 degrees C for 10 min (WB) on the content and leaching of residual compounds, degree of conversion, flexural strength, and hardness of hard ...