Evaluation of geomembrane UV degradation using melt flow index and oxidative induction time tests
(Zhejiang Univ Press, 2008-01-01)
Many factors such as the sunlight, intensity of radiation, temperature, and moisture may influence the degradation process of geosynthetics. UV stabilizers are used especially in polyolefin geomembrane to prevent the ...
Evaluation of geomembrane UV degradation using melt flow index and oxidative induction time tests
(Zhejiang Univ Press, 2008-01-01)
Many factors such as the sunlight, intensity of radiation, temperature, and moisture may influence the degradation process of geosynthetics. UV stabilizers are used especially in polyolefin geomembrane to prevent the ...
Evaluation of geomembrane UV degradation using melt flow index and oxidative induction time tests
(2008-01-01)
Many factors such as the sunlight, intensity of radiation, temperature, and moisture may influence the degradation process of geosynthetics. UV stabilizers are used especially in polyolefin geomembrane to prevent the ...
Degradação de geomembranas de polietileno de alta densidade (HDPE) após exposição à intempérie e lixívia
(2010)
This paper presents some results of MFI and OIT tests performed on HDPE geomembranes of 0,8 and 2,5 mm that were exposed to weathering effects and leachate after 30 months (2,5 years). The aim of this work is the evaluation ...
Evaluation of geomembrane UV degradation using melt flow index and oxidative induction time tests
(Zhejiang Univ Press, 2014)
The Effects of Weathering Exposure on the Physical, Mechanical, and Thermal Properties of High-density Polyethylene and Poly (Vinyl Chloride)
(Univ Fed Sao Carlos, Dept Engenharia Materials, 2013-11-01)
This paper presents results describing the physical, mechanical, and thermal properties (melt flow index - MFI and oxidative induction time - OIT) of high density polyethylene and poly (vinyl chloride) after weathering ...
The Effects of Weathering Exposure on the Physical, Mechanical, and Thermal Properties of High-density Polyethylene and Poly (Vinyl Chloride)
(Univ Fed Sao Carlos, Dept Engenharia Materials, 2014)
The Effects of Weathering Exposure on the Physical, Mechanical, and Thermal Properties of High-density Polyethylene and Poly (Vinyl Chloride)
(Univ Fed Sao Carlos, Dept Engenharia Materials, 2014)