Evaluation of mechanical and thermal properties after chemical degradation of PVC and HDPE geomembranes
(2013-06-10)
Chemical compatibility between geomembranes and site-specific waste liquids should be assessed since the waste liquids are highly complex mixtures. This paper presents some considerations about the chemical compatibility ...
Thermal degradation of geomembranes after exposure to heat
(Millpress Science Publishers, 2006-01-01)
HDPE and PVC geomembranes are sensitive to changes in their properties when in contact with high temperatures. The effects of hot temperature on polymeric geomembranes are assessed by the ASTM D794 and ASTM D5721.This paper ...
Thermal degradation of geomembranes after exposure to heat
(Millpress Science Publishers, 2006-01-01)
HDPE and PVC geomembranes are sensitive to changes in their properties when in contact with high temperatures. The effects of hot temperature on polymeric geomembranes are assessed by the ASTM D794 and ASTM D5721.This paper ...
Evaluation of mechanical and thermal properties after chemical degradation of PVC and HDPE geomembranes
(2013-06-10)
Chemical compatibility between geomembranes and site-specific waste liquids should be assessed since the waste liquids are highly complex mixtures. This paper presents some considerations about the chemical compatibility ...
Thermo-gravimetric analysis (TGA) after different exposures of high density polyethylene (HDPE) and poly vinyl chloride (PVC) geomembranes
(2012-12-03)
This paper presents the results of thermogravimetric analysis (TGA) tests in PVC (1.0; 2.0 mm) and HDPE (0.8; 2.5 mm) geomembranes exposed to weathering and leachate after 30 months. The aim of this paper is the comparison ...
Thermo-gravimetric analysis (TGA) after different exposures of high density polyethylene (HDPE) and poly vinyl chloride (PVC) geomembranes
(2012-12-03)
This paper presents the results of thermogravimetric analysis (TGA) tests in PVC (1.0; 2.0 mm) and HDPE (0.8; 2.5 mm) geomembranes exposed to weathering and leachate after 30 months. The aim of this paper is the comparison ...
Influence of the degradation on the stress cracking values of high density polyethylene (HDPE) geomembranes after different exposures
(2012-12-03)
This paper presents results from stress cracking (SC) tests performed in both fresh and exposed high density polyethylene (HDPE) geomembranes (GM). The HDPE GMs were exposed to ultraviolet radiation, thermal aging (air ...
Influence of the degradation on the stress cracking values of high density polyethylene (HDPE) geomembranes after different exposures
(2012-12-03)
This paper presents results from stress cracking (SC) tests performed in both fresh and exposed high density polyethylene (HDPE) geomembranes (GM). The HDPE GMs were exposed to ultraviolet radiation, thermal aging (air ...