Nanoparticle characterization of Er-doped SnO2 pellets obtained with different pH of colloidal suspension
(2013-08-28)
SnO2:2 at. %Er xerogel samples were obtained by sol-gel technique from colloidal suspensions with distinct pHs. The evaluation of critical regions inside the nanocrystallite is fundamental for the interpretation of the ...
Nanoparticle characterization of Er-doped SnO2 pellets obtained with different pH of colloidal suspension
(2013-08-28)
SnO2:2 at. %Er xerogel samples were obtained by sol-gel technique from colloidal suspensions with distinct pHs. The evaluation of critical regions inside the nanocrystallite is fundamental for the interpretation of the ...
Determinação das condições de ataque químico seletivo para alteração de composição superficial de ligas de ouro
(Universidade Estadual Paulista (Unesp), 2003-03)
O ataque químico seletivo para alteração da composição superficial de ligas de ouro, é um processo que permite retirar os elementos de liga, de uma camada superficial de uma peça confeccionada com liga de ouro, produzindo ...
Determinação das condições de ataque químico seletivo para alteração de composição superficial de ligas de ouro
(Universidade Estadual Paulista (Unesp), 2003-03)
O ataque químico seletivo para alteração da composição superficial de ligas de ouro, é um processo que permite retirar os elementos de liga, de uma camada superficial de uma peça confeccionada com liga de ouro, produzindo ...
Determinação das condições de ataque químico seletivo para alteração de composição superficial de ligas de ouro
(Universidade Estadual Paulista (UNESP), 2014)
Quantification of casting sking in ductile and compacted graphite irons and its effect on tensile properties
(Springer, 2009-08)
The mechanical properties of ductile iron (DI) and compacted graphite iron (CGI) are measured and reported on standard machined specimens (as per ASTM). However, most castings retain most of the as-cast surface. This surface ...
Compositional and structural changes at the anodic surface of thermally poled soda-lime float glass
(American Institute of Physics (AIP), 2008-09-01)
Applying high dc electric fields at elevated temperatures on silicate glasses results in displacement of ions, causing compositional and structural changes in the anodic surface. In this work, the ionic displacement was ...
Compositional and structural changes at the anodic surface of thermally poled soda-lime float glass
(American Institute of Physics (AIP), 2008-09-01)
Applying high dc electric fields at elevated temperatures on silicate glasses results in displacement of ions, causing compositional and structural changes in the anodic surface. In this work, the ionic displacement was ...