Boundary element analysis of fatigue crack propagation micromechanisms in austempered ductile iron
(Elsevier, 2001-07-01)
The Dual Boundary Element Method (DBEM) is used in this work to model the micro mechanics of fatigue crack propagation in austempered ductile iron (ADI). Emphasis is put in devising accurate procedures for the evaluation ...
High-Temperature Corrosion Fatigue of a Ferritic Ductile Cast Iron in Inert and Corrosive Environments at 700ºC
(INTEMA - UNMdP-CONICET, 2014)
High-Temperature Corrosion Fatigue of a Ferritic Ductile Cast Iron in Inert and Corrosive Environments at 700ºC
(INTEMA - UNMdP-CONICET, 2014)
Embrittlement of case hardened steel chain link
(PERGAMON-ELSEVIER SCIENCE LTD, 2009)
Various steel chain links presented cracking during their manufacturing process, which includes induction case hardening and electrogalvanizing steps. Fractographic examination of the exposed crack surfaces revealed ...
Damage evolution during tensile test of austempered ductile iron partially austenized
(Wiley, 2020-02)
The goal of this work is to analyze the damage evolution at microstructural scale of an austempered ductile iron partially austenized during tensile loading. The analysis is carried out by means of step-by-step tensile ...
Influence of Microstructures on Polarization Resistance and Hydrogen-Induced Cracking of a Micro-Alloyed Steel Submitted to Different Cooling Rates
(JOURNAL IRON STEEL RESEARCH EDITORIAL BOARD, 2011)
The effect of different microstructures on the polarization resistance (Rp) and the hydrogen-induced cracking (HIC) of a micro-alloyed steel austenitized and submitted to different cooling rates was studied. Samples 19.1 ...