Thermal behavior of the Cu-10 mass%Al and Cu-10 mass%Al-4 mass%Ag alloys
(Kluwer Academic Publ, 2004-01-01)
The thermal behavior of the Cu-10 mass%Al and Cu-10 mass% Al-4 mass%Ag alloys was studied using classical differential thermal analysis (DTA), optical microscopy (OM) and X-ray diffractometry (XRD). The DTA curves were ...
Thermal behavior of the Cu-10 mass%Al and Cu-10 mass%Al-4 mass%Ag alloys
(Kluwer Academic Publ, 2004-01-01)
The thermal behavior of the Cu-10 mass%Al and Cu-10 mass% Al-4 mass%Ag alloys was studied using classical differential thermal analysis (DTA), optical microscopy (OM) and X-ray diffractometry (XRD). The DTA curves were ...
Precipitation reaction in alpha-Cu-Al-Ag alloys
(Rede Latino-Americana de Materiais, 2011-01-01)
The Ag-rich precipitates formation reaction in the Cu-9.22%at. Al-4.66%at. Ag, Cu-9.31%at. Al-5.83%at. Ag and Cu-9.37%at. Al-7.08%at. Ag alloys was studied using microhardness change measurements with temperature and time, ...
Precipitation reaction in alpha-Cu-Al-Ag alloys
(Rede Latino-Americana de Materiais, 2011-01-01)
The Ag-rich precipitates formation reaction in the Cu-9.22%at. Al-4.66%at. Ag, Cu-9.31%at. Al-5.83%at. Ag and Cu-9.37%at. Al-7.08%at. Ag alloys was studied using microhardness change measurements with temperature and time, ...
Kinetics of Ag-rich precipitates formation in Cu-Al-Ag alloys
(Elsevier B.V., 2004-06-15)
The kinetics of Ag-rich precipitates formation in the Cu-2 wt.% Al alloy with additions of 2, 4, 6, 8, 10 and 12 wt.% Ag was studied using microhardness changes with temperature and time, differential scanning calorimetry ...
Kinetics of Ag-rich precipitates formation in Cu-Al-Ag alloys
(Elsevier B.V., 2004-06-15)
The kinetics of Ag-rich precipitates formation in the Cu-2 wt.% Al alloy with additions of 2, 4, 6, 8, 10 and 12 wt.% Ag was studied using microhardness changes with temperature and time, differential scanning calorimetry ...
Reação de precipitação de Ag na liga Cu-8%Al-6%Ag
(Editora Unesp, 2014)
Ag-rich phase precipitation in the Cu-9 mass% Al alloy with Ag additions
(Springer, 2009-07-01)
The Ag-rich phase precipitation in the Cu-9 mass% Al was studied using differential scanning calorimetry (DSC), X-ray diffractometry (XRD) and scanning electron microscopy (SEM). The results indicated that Ag additions did ...
Ag-rich phase precipitation in the Cu-9 mass% Al alloy with Ag additions
(Springer, 2009-07-01)
The Ag-rich phase precipitation in the Cu-9 mass% Al was studied using differential scanning calorimetry (DSC), X-ray diffractometry (XRD) and scanning electron microscopy (SEM). The results indicated that Ag additions did ...
Reação de precipitação de Ag na liga Cu-8%Al-6%Ag
(2008-01-01)
Ag precipitation reaction in the Cu-8wt.%Al-6wt.%Ag alloys was studied using microhardness measurements with temperature and ageing time, X-ray diffraction patterns (DRX), differential scanning calorimetry (DSC) and scanning ...