Fatigue life and failure modes of crowns systems with a modified framework design
(ELSEVIER SCI LTD, 2010)
Objectives: To evaluate the effect of framework design on the fatigue life and failure modes of metal ceramic (MC, Ni-Cr alloy core, VMK 95 porcelain veneer), glass-infiltrated alumina (ICA, In-Ceram Alumina/VM7), and ...
EFFECT OF CADMIUM COATING ON THE FATIGUE STRENGTH OF AISI 4140 STEEL USED IN OIL AND GAS COMPANY
(Inegi-feup, 2017-01-01)
The influence of electrodeposited coating of cadmium on AISI 4140 steel has been studied at room temperature in axial fatigue. Axial fatigue testing was performed using studs at base metal and cadmium coated conditions. ...
Evaluation of an electroless nickel interlayer on the fatigue & corrosion strength of chromium-plated AISI 4340 steel
(Amer Electroplaters Soc Inc, 2001-04-01)
Despite the fact that chromium electrodeposition results in protection against wear and corrosion, combined with chemical resistance and good lubricity, the reduction in fatigue strength of base metal and environmental ...
Evaluation of an electroless nickel interlayer on the fatigue & corrosion strength of chromium-plated AISI 4340 steel
(Amer Electroplaters Soc Inc, 2001-04-01)
Despite the fact that chromium electrodeposition results in protection against wear and corrosion, combined with chemical resistance and good lubricity, the reduction in fatigue strength of base metal and environmental ...
Microstructural effects on fatigue crack growth behavior of a microalloyed steel
(2010-04-01)
Thermal transformations on microalloyed steels can produce multiphase microstructures with different amounts of ferrite, martensite, bainite and retained austenite. These different phases, with distinct morphologies, are ...
Microstructural effects on fatigue crack growth behavior of a microalloyed steel
(2010-04-01)
Thermal transformations on microalloyed steels can produce multiphase microstructures with different amounts of ferrite, martensite, bainite and retained austenite. These different phases, with distinct morphologies, are ...
Low-cycle fatigue modelling supported by strain energy density-based Huffman model considering the variability of dislocation density
(2021-10-01)
The fatigue crack initiation and propagation phases have been widely studied by the scientific community. There are several models to describe low-cycle fatigue behaviour based on strain damage criteria, but the most widely ...
Hygrothermal Aging Effect on Fatigue Behavior of GLARE
(Sage Publications Ltd, 2014)