Obtención de resinas fenólicas termoestables de lignina extraída del bagazo de la caña de azúcar.
Obtención de resinas fenólicas termoestables de lignina extraída del bagazo de la caña de azúcar.
Autor
León, Sandra
Sanabria, Franklin
Institución
Resumen
Polymerized thermostable resins were obtained from legnine, extracted from sugar cane bagasse. This was done in two stages: The lignine is phenolized by reaction in an acid medium.The lignine is then reacted during the molding operation, with hexamethylentetraamine, that acts like a crosslinking agent. Some properties of the synthetized resins were determinate; it a was found that the best formulation consist of 46,0% of resin (phenollignine), 34,5% of bagasse, 13,8% of hexamethylentetraamine, 3,7% of magnesium oxide and 2,0% of zinc stearate. Se obtuvieron resinas termoestabes por polimerización de lignina extraída del bagazo de caña de azúcar en dos etapas: en primer lugar se fenoliza la lignina por reacción en medio ácido y luego se hace reaccionar, durante la operación de molde, con hexametilentetramina que actúa como agente entrecruzador. Se determinaron algunas propiedades de las resinas sintetizadas y se encontró que la mejor formulación consiste en 46,0% de resina (fenol-linina), 34,5% de bagazo, 13,8% de hexametilentetramina, 3,7% de óxido de magnesio y 2,0% de estearato de zinc.