Comparison of the biocompatibility of grey mineral trioxide aggregate and sealapex plus zinc oxide in rat subcutaneous tissue
Registro en:
VITA, W. et al. Comparison of the biocompatibility of grey mineral trioxide aggregate and sealapex plus zinc oxide in rat subcutaneous tissue. Clinical and Laboratorial Research in Dentistry, v. 21, n. 3, p. 136-144, 2015.
2357-8041
Autor
Vita, Waldécio
Reis, Mitermayer Galvão dos
Santos, Théo Araujo
Carvalho, Ana Maria
Mota, Cristina
Ramos, Eduardo Antônio Gonçalves
Resumen
O objetivo deste estudo foi comparar a biocompatibilidade do agregado trióxido mineral
cinza (GMTA) com o Sealapex acrescido de óxido de zinco (Sealapex/ZnO) em tecidos subcutâneos de ratos. Métodos: Tubos de polietileno
preenchidos com os materiais testados foram implantados no tecido conjuntivo de ratos. Os animais do grupo controle receberam
tubos vazios. Amostras de tecido foram coletadas após 7, 60 e 90 dias e coradas com hematoxilina-eosina, picrosirius-fast green e von
Kossa para a análise morfológica. A resposta do tecido conjuntivo aos materiais implantados foi avaliada descritiva e semi-quantitativa,
marcando o grau de inflamação, formação de tecido de granulação, fibrose e calcificação. Resultados: Análise do grupo GMTA, ao longo
do tempo, revelou inflamação mais intensa com 7 dias do que com 60 dias (p <0,05). No grupo Sealapex/ZnO, o tecido de granulação
foi mais abundante com 7 dias do que com 60 dias (p <0,05). Quanto a grau de calcificação, granulações von Kossa-positivas foram observadas
nos grupos GMTA e Sealapex/ZnO em todos os períodos de tempo estudados. No grupo Sealapex/ZnO, a calcificação foi mais
aparente com 60 dias do que com 7 dias (p <0,05). Relevância: Este estudo demonstra que todos os materiais testados promovem
reações teciduais semelhantes. Centro de Pesquisa Gonçalo Moniz, Fundação Oswaldo Cruz, and Fundação de Amparo a Pesquisa da Bahia (Salvador, Bahia, Brazil) The aim of this study was to compare the subcutaneous tissue response to grey mineral trioxide aggregate
and white Sealapex plus zinc oxide. Methods: Polyethylene tubes filled with the tested materials were implanted in
the connective tissue of rats. Control animals received empty tubes. Tissue samples were collected after 7, 60, and 90
days and stained with hematoxylin-eosin, picrosirius-fast green, and von Kossa stain for morphological analysis. The
connective tissue response to the implanted materials was evaluated descriptively and semi-quantitatively by scoring
the degree of inflammation, granulation tissue formation, fibrosis, and calcification. Results: Examinations of the grey
mineral trioxide aggregate group over time revealed more intense inflammation at 7 days than at 60 days (P<.05). In
the Sealapex plus zinc oxide group, granulation tissue was more abundant at 7 days than at 60 days (P < .05). Regarding
calcification, von Kossa-positive granules were observed in the grey mineral trioxide aggregate and Sealapex plus zinc
oxide groups at all time points studied. In the Sealapex plus zinc oxide group, calcification was more apparent at 60 days
than at 7 days (P < .05). Relevance: This study demonstrates that all tested materials result in similar tissue reactions.