SÍNTESE E CARACTERIZAÇÃO DE ESPUMAS VÍTREAS CONTENDO TiO2 E UTILIZANDO HIDRÓXIDO DE SÓDIO COMO AGENTE ESPUMANTE
Registro en:
BENTO, André César. SÍNTESE E CARACTERIZAÇÃO DE ESPUMAS VÍTREAS CONTENDO TiO2 E UTILIZANDO HIDRÓXIDO DE SÓDIO COMO AGENTE ESPUMANTE. 2012. 46 f. Dissertação (Mestrado em Desenvolvimento e Caracterização de Materiais) - UNIVERSIDADE ESTADUAL DE PONTA GROSSA, Ponta Grossa, 2012.
Autor
Bento, André César
Institución
Resumen
In this work, the effect of sodium hydroxide as a glass foaming agent using glass waste in the foam formulation was performed. During the synthesis process, the variation of temperature, heating rate and sintering time was investigated. Sample density and average pore sizes were estimated using mercury porosimetry. The morphology of the glass foams were evaluated using scanning electron microscopy, phase formation was studied using X-ray diffraction, and chemical composition was estimated using X-ray fluorescence. As a result, glass foam with hierarchical density. Neste trabalho foi realizado um estudo sobre a ação do hidróxido de sódio como agente formador de espuma vítrea usando resíduos de vidro em sua composição. Para a síntese, investigou-se a variação da temperatura, da taxa de aquecimento e do tempo de sinterização. Utilizando-se a técnica de porosimetria de mercúrio, para estimar a densidade e o tamanho médio de poros. A morfologia das espumas vítreas foi avaliada através da microscopia eletrônica de varredura de alta resolução (FEG) e as fases das espumas vítreas foram caracterizadas pelas técnicas de difração de raios X e a composição química estimada usando fluorescência de raios X.