Effect of PAA-coated magnetic nanoparticles on the performance of PVA-based hydrogels developed to be used as environmental remediation devices
Fecha
2019-03Registro en:
Sanchez, Laura Mabel; Actis, Daniel Guillermo; Gonzalez, Jimena Soledad; Mendoza Zélis, Pedro; Alvarez, Vera Alejandra; Effect of PAA-coated magnetic nanoparticles on the performance of PVA-based hydrogels developed to be used as environmental remediation devices; Springer; Journal of Nanoparticle Research; 21; 64; 3-2019; 1-16
1388-0764
CONICET Digital
CONICET
Autor
Sanchez, Laura Mabel
Actis, Daniel Guillermo
Gonzalez, Jimena Soledad
Mendoza Zélis, Pedro
Alvarez, Vera Alejandra
Resumen
In the present work, the effect of the incorporation of polyacrylic acid (PAA)–coated magnetic nanoparticles (MNPs) on the performance of polyvinyl alcohol (PVA)–based hydrogels for water remediation was studied. Ferrogels from PVA and PAA-coated MNPs were prepared through the ecocompatible freezing–thawing physical cross-linking method, and then they were completely characterized. Two different lab-made PAA-coated iron oxide MNPs, characterized in a previous work, were prepared by coprecipitation method from two different low PAA molecular weights, Mw 1800 g/mol and 5000 g/mol. The effect of MNP content and the PAA Mw on ferrogel final properties was determined. In addition, adsorption of methylene blue (MB) and cadmium (Cd+2) was carried out to analyze the possible application of the developed materials as environmental remediation devices. The capture of a ferrogel by an external field occurs due to the force that the field gradient exerts on single magnetic particles, which is then transferred onto the polymer matrix. This force was measured as a function of the distance to a permanent magnet, and the condition to magnetically recover the sample was established. The results obtained demonstrated that the ferrogels presented in this work are able to adsorb heavy metals and then be magnetically separated.