Visible-light photocatalysis with bismuth titanate (Bi12TiO20) particles synthesized by the oxidant peroxide method (OPM)
Fecha
2015-05-01Registro en:
Ceramics International, v. 41.
0272-8842
10.1016/j.ceramint.2015.06.024
2-s2.0-84932181660
2-s2.0-84932181660.pdf
Autor
Universidade Federal de São Carlos (UFSCar)
Universidade Estadual Paulista (Unesp)
Institución
Resumen
In this paper, we have successfully synthesized high quality single crystalline bismuth titanate with sillenite (Bi12TiO20) phase by the oxidant peroxide method (OPM). The structures of precipitate and calcined materials were characterized by X-ray diffraction (XRD), UV-vis diffuse reflectance spectra (DRS), X-ray photoluminescence (PL) spectroscopy, thermogravimetry analysis (TG), differential scanning calorimetry (DSC) Fourier transform infrared spectroscopy (FTIR), transmission electron microscope (TEM), scanning electron microscopy (SEM) and nitrogen adsorption/desorption. The XRD analysis showed that the calcination temperature of 500°C and time of 1h was found to be sufficient to produce Bi12TiO20 powder and the DRS confirmed that the photoresponse of the prepared bismuth titanate extended to the visible light region at about 465nm representing a possible photoactivity under solar irradiation. The photocatalytic activities were verified through the photocatalytic degradation of rhodamine b (RhB) as a model compound under visible light irradiation. It was found that the material calcined at 400°C exhibits good photocatalytic activity compared to commercial TiO2, the kinetic rate constant over 400°C is 0.006min-1, which is 9.4 times higher than commercial TiO2. The higher photocatalytic activity of this material is mainly attributed to an increase in the extension of its optical absorption spectrum, as compared to TiO2.