Characterization of superconducting BSCCO/CaSiO3 and BSCCO/CaZrO3 Ag PIT wires

dc.contributorUniversidade Estadual Paulista (Unesp)
dc.date.accessioned2016-03-02T13:03:31Z
dc.date.available2016-03-02T13:03:31Z
dc.date.created2016-03-02T13:03:31Z
dc.date.issued2014
dc.identifierAdvanced Materials Research, v. 975, p. 106-110, 2014.
dc.identifier1662-8985
dc.identifierhttp://hdl.handle.net/11449/135606
dc.identifier10.4028/www.scientific.net/AMR.975.106
dc.identifier8506867595279427
dc.description.abstractThe addition of two compounds, calcium silicate and calcium zirconate was tested, in the preparation of Bi: 2212 silver sheathed wires by powder-in-tube method, which were successfully tested previously in processing chips. The wires were treated in an atmosphere of O2/Ar using partial melting method. The characterizations were structural and on their electrical and magnetic properties. As the results, transition temperatures were higher than the expected for this stage, ranged from 105K (BSCCO880) to 116K (+Si883). The critical current densities encountered in transport and magnetization measurements were improved in comparison with the wires without addition.
dc.languageeng
dc.relationAdvanced Materials Research
dc.relation0,121
dc.rightsAcesso restrito
dc.sourceCurrículo Lattes
dc.subjectBSCCO Wire
dc.subjectCaSiO3 addition to BSCCO
dc.subjectCaZrO3 addition to BSCCO
dc.subjectElectrical measurements
dc.subjectMagnetic measurements
dc.subjectMicrostructure
dc.subjectSuperconductor
dc.titleCharacterization of superconducting BSCCO/CaSiO3 and BSCCO/CaZrO3 Ag PIT wires