The surface treatment influence on the fatigue crack propagation of Al 7050-T7451 alloy
(Elsevier B.V. Sa, 2009-04-15)
The objective of this research is to evaluate 100 mu m, thickness hard chromium electroplated coating on the fatigue crack propagation of Al 7050-T7451 alloy. The shot peening process was carried out to create residual ...
The surface treatment influence on the fatigue crack propagation of Al 7050-T7451 alloy
(Elsevier B.V. Sa, 2009-04-15)
The objective of this research is to evaluate 100 mu m, thickness hard chromium electroplated coating on the fatigue crack propagation of Al 7050-T7451 alloy. The shot peening process was carried out to create residual ...
The surface treatment influence on the fatigue crack propagation of Al 7050-T7451 alloy
(Elsevier B.V. Sa, 2014)
Coating residual stress effects on fatigue performance of 7050-T7451 aluminum alloy
(Elsevier B.V., 2007-10-15)
The tendency of the aircraft industry is to enhance customer value by improving performance and reducing environmental impact. In view of availability, aluminum alloys have a historically tendency to faster insertion due ...
Coating residual stress effects on fatigue performance of 7050-T7451 aluminum alloy
(Elsevier B.V., 2007-10-15)
The tendency of the aircraft industry is to enhance customer value by improving performance and reducing environmental impact. In view of availability, aluminum alloys have a historically tendency to faster insertion due ...
Coating residual stress effects on fatigue performance of 7050-T7451 aluminum alloy
(Elsevier B.V., 2014)
CARACTERIZAÇÃO MICROESTRUTURAL DAS PARTÍCULAS DE SEGUNDA FASE DE UMA LIGA DE ALUMÍNIO AA7050 NAS CONDIÇÕES T7451, T6 E T6I4-65CARACTERIZAÇÃO MICROESTRUTURAL DAS PARTÍCULAS DE SEGUNDA FASE DE UMA LIGA DE ALUMÍNIO AA7050 NAS CONDIÇÕES T7451, T6 E T6I4-65
(UNIVERSIDADE ESTADUAL DE PONTA GROSSABRDesenvolvimento e Caracterização de MateriaisPrograma de Pós-Graduação em Engenharia e Ciências de MateriaisUEPG, 2017)
Estudo sobre o tratamento térmico de envelhecimento interrompido T6I4-65 e influência na propagação de trinca por fadiga em uma liga de alumínio AA7050
(UNIVERSIDADE ESTADUAL DE PONTA GROSSABRDesenvolvimento e Caracterização de MateriaisPrograma de Pós-Graduação em Engenharia e Ciências de MateriaisUEPG, 2017)