Structural modifications in stretch-induced crystallization in PVDF films as measured by small-angle X-ray scattering
(Wiley-Blackwell, 2012-07-05)
The nanostructure of stretched and nonstretched PVDF samples was studied by small-angle X-ray scattering (SAXS). The crystallinity of the samples was determined by wide-angle X-ray diffraction (WAXD) and differential ...
Structural modifications in stretch-induced crystallization in PVDF films as measured by small-angle X-ray scattering
(Wiley-Blackwell, 2012-07-05)
The nanostructure of stretched and nonstretched PVDF samples was studied by small-angle X-ray scattering (SAXS). The crystallinity of the samples was determined by wide-angle X-ray diffraction (WAXD) and differential ...
Performance of annealed hybride silicon heterojunctions: a numerical computer study
(American Institute of Physics, 2005-01)
The performance of the standard hydrogenated amorphous silicon carbon–crystalline silicon solar cell is extensively compared with the performance of a hybrid structure subjected to a high-temperature annealing processing. ...
Silanization effect on the photoluminescence characteristics of crystalline and amorphous silicon nanoparticles
(Royal Society of Chemistry, 2013-05)
Silicon nanoparticles synthesized by two different methods, were surface modified with 3-mercaptopropyltrimethoxysilane. The particles of ~ 2 nm size, exhibit photoluminescence (PL) in the UV-Vis range of the spectrum. The ...
Laser crystallization and structuring of amorphous germanium
(Amer Inst PhysicsWoodbury, 1997)
Morphological transformation and kinetic analysis in the aluminum-mediated a-Si:H crystallization
(2012-12-17)
We analyzed the amorphous–crystalline morphological transformation of a-Si:H films caused by applying an annealing treatment to
the Al/a-Si:H system at low temperature (250 C) during several hours. Optical micrographs ...
Morphological transformation and kinetic analysis in the aluminum-mediated a-Si:H crystallization
(2012-11-23)
We analyzed the amorphous–crystalline morphological transformation of a-Si:H films caused by applying an annealing treatment to
the Al/a-Si:H system at low temperature (250 C) during several hours. Optical micrographs ...
Morphological transformation and kinetic analysis in the aluminum-mediated a-Si:H crystallization
(2012-11-26)
We analyzed the amorphous–crystalline morphological transformation of a-Si:H films caused by applying an annealing treatment to
the Al/a-Si:H system at low temperature (250 C) during several hours. Optical micrographs ...