Effect of home-bleaching gels modified by calcium and/or fluoride and the application of nano-hydroxyapatite paste on in vitro enamel erosion susceptibility
Registro en:
Acta Odontologica Scandinavica, p. 1-6, 2015.
1502-3850
10.3109/00016357.2015.1053150
26083582
Autor
Santos, Luciana Floriani Thives Freitas
Torres, Carlos Rocha Gomes
Caneppele, Taciana Marco Ferraz
Magalhães, Ana Carolina
Borges, Alessandra Buhler
Resumen
This in vitro study compared the effect of bleaching agents modified by the addition of calcium and/or fluoride and the application of a nano-hydroxyapatite paste after bleaching, on the susceptibility of enamel to erosion. Bovine enamel cylindrical samples (3 mm diameter) were assigned to six groups (n = 20 specimens/group) according to the bleaching agent: no bleaching (C-control), 7.5% hydrogen peroxide gel (HP), HP with 0.5% calcium gluconate (HP+Ca), HP with 0.2% sodium fluoride (HP+F), HP with calcium and fluoride (HP+Ca+F) and HP followed by the application of a nano-hydroxyapatite agent (HP+NanoP). The gels were applied on the enamel surface (1 h) followed by cyclic erosive challenges (Sprite Zero®-2 min), for 14 days. The paste was applied after bleaching for 5 min (HP+NanoP). The enamel surface alteration was measured by contact profilometry (µm) (after 7 and 14 days). C-control (mean ± SD: 2.29 ± 0.37 at 7 days/4.86 ± 0.72 at 14 days) showed significantly lower loss compared to the experimental groups. HP+Ca (3.34 ± 0.37/6.75 ± 1.09) and HP+F (4.49 ± 0.92/7.61 ± 0.90) presented significantly lower enamel loss than HP (4.18 ± 0.50/10.30 ± 1.58) only for 14 days and HP+Ca+F (4.92 ± 1.03/8.12 ± 1.52) showed values similar to the HP+F group. The HP+NanoP (5.51 ± 1.04/9.61 ± 1.21) resulted in enamel loss similar to the HP after 14 days. It was found that 7.5% hydrogen peroxide increased the susceptibility of enamel to erosion. The addition of calcium or fluoride to the bleaching gel reduced the erosion effect, while the nano-hydroxyapatite agent did not provide any protective effect.