Tricot stitched carbon fiber reinforced polymer composite laminates manufactured by resin transfer molding process: C-scan and flexural analysis

dc.contributorUniversidade Estadual Paulista (UNESP)
dc.creatorShiino, Marcos Yutaka
dc.creatorHilario Cioffi, Maria Odila
dc.creatorJacobus Voorwald, Herman Cornelis
dc.creatorOrtiz, Edmundo Cabral
dc.date2014-12-03T13:11:49Z
dc.date2016-10-25T20:15:15Z
dc.date2014-12-03T13:11:49Z
dc.date2016-10-25T20:15:15Z
dc.date2013-06-01
dc.date.accessioned2017-04-06T06:35:06Z
dc.date.available2017-04-06T06:35:06Z
dc.identifierJournal Of Composite Materials. London: Sage Publications Ltd, v. 47, n. 14, p. 1695-1703, 2013.
dc.identifier0021-9983
dc.identifierhttp://hdl.handle.net/11449/113593
dc.identifierhttp://acervodigital.unesp.br/handle/11449/113593
dc.identifier10.1177/0021998312450928
dc.identifierWOS:000320023400002
dc.identifierhttp://dx.doi.org/10.1177/0021998312450928
dc.identifier.urihttp://repositorioslatinoamericanos.uchile.cl/handle/2250/924334
dc.descriptionNC2 (R) tricot stitched carbon preform has been tested to evaluate its potential application in aircraft structures. It is one in a range of stitched fabric group, specially developed by Hexcel Composites, designed to be processed with a RTM6 monocomponent resin. This article aims to evaluate the tricot stitched fabric behavior towards resin flow front in resin transfer molding process, its mechanical performance in bending test, and its structure during C-scan non-destructive inspection. Flexural performance of the laminates and the scatter of the results corresponded well with C-scan ultrasonic maps, where resin pockets near the stitches were distinguished. The fracture area visualization, via photography and scanning electron microscopy techniques, aided to find a few flaws between the stitch yarns, which conducted to a larger scatter of the flexural rupture strength results.
dc.descriptionFundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)
dc.languageeng
dc.publisherSage Publications Ltd
dc.relationJournal of Composite Materials
dc.rightsinfo:eu-repo/semantics/closedAccess
dc.subjectBending test
dc.subjectC-scan test
dc.subjectresin transfer molding
dc.subjectstitched fabric
dc.titleTricot stitched carbon fiber reinforced polymer composite laminates manufactured by resin transfer molding process: C-scan and flexural analysis