The purpose of this study was to evaluate the sliding wear resistance of the A36 steel coated with Inconel 625 in comparison to another two coatings: 1- 316 stainless steel and 2- Inconel 625 superimposed on 316 stainless steel. The samples were sanded and polished. Tests were performed in the Universal Plint® Tribometer (model TE 67 Plint and Partners LDT) using the reciprocating configuration. The test load was set to 21.5 N and the counter body was 10 mm steel beads. Three tests were performed in each sample. Despite having a coefficient of friction higher than the sample with stainless steel coating, the Inconel 625 coating sample presented a lower wear rate.Trabalho de Conclusão de Curso (Graduação)O presente trabalho objetivou avaliar a resistência ao desgaste por deslizamento do aço A36 revestido com Inconel 625, comparando com outros dois revestimentos, um de aço inoxidável 316 e outro de Inconel 625 sobreposto ao aço inoxidável 316. As amostras foram lixadas e polidas. Para realizar os ensaios, foi utilizado o Tribômetro Universal Plint® (modelo TE 67 Plint and Partners LDT) na configuração movimento alternado. A carga de teste utilizada foi de 21,5 N e o contra corpo adotado foram esferas de 10 mm. Foram feitos três ensaios para cada amostra. Após a realização dos testes, foi verificado que, apesar de possuir um coeficiente de atrito maior que a amostra com revestimento de aço inox, a amostra de revestimento com Inconel 625 apresenta menor desgaste.