Zeolitic materials were synthesized using as main source of silicon and aluminum an industrial waste generated during the processing of kaolin for paper coating, the starting material and formed phases as reaction products were characterized by XRD, SEM and DRIFT. The synthesis process occurred in hydrothermal conditions and the effects, time-temperature, as well as the relations Si/Al and Na/Al were considered. The results show that in the methodology developed from kaolin waste, initially calcined at 700 ºC for 2 h, subjected then reaction in alkaline medium at 90 ºC for 48 h in presence of additional silica was obtained faujasite-type zeolite with good crystallinity as phase predominant in the synthesis product.Materiais zeolíticos foram sintetizados utilizando como fonte principal de silício e alumínio um rejeito industrial gerado durante o beneficiamento do caulim para cobertura de papel; o material de partida e as fases formadas como produtos de reação foram caracterizados por difração de raios X, microscopia eletrônica de varredura e espectroscopia de refletância difusa no infravermelho com transformada de Fourier. O processo de síntese ocorreu em condições hidrotermais através de autoclavagem estática e os efeitos tempo-temperatura, assim como também as relações Si/Al e Na/Al foram considerados. Os resultados mostram que na metodologia desenvolvida com o rejeito de caulim, inicialmente calcinado a 700 ºC por 2 h, submetido em seguida à reação em meio alcalino a 90 ºC por 48 h na presença de uma fonte adicional de sílica foi obtida zeólita do tipo faujasita com boa cristalinidade como fase predominante no produto de síntese.