Caracterização mineralógica de azulejos de Salvador e Belém dos séculos XVI, XVII e XIX
Registro en:
0370-4467
Autor
SANJAD, Thais Alessandra Bastos Caminha
ANGÉLICA, Rômulo Simões
OLIVEIRA, Mário Mendonça de
COSTA, Walmeire Alves de Melo
Institución
Resumen
The present article is a study about the mineralogical composition of ancient tiles from centuries XVI, XVII and XIX, found in Belém and Salvador, in order to interpret the possible raw material and burning temperature. Quartz was identified in all samples. Other crystalline phases found are mullite, cristobalite, calcite, anorthite, hematite, gehlenite, diopside and wollastonite. Based on the probable raw material and probable burning temperature it was possible to organize the samples into three groups: group 1 - kaolinite and quartz, T between 1200º and 1728º C; group 2 - kaolinite, calcite and/or dolomite and iron oxide or hydroxide, T between 900º e 1200ºC; group 3 - quartz, clay minerals (probably kaolinite), calcite and/or dolomite, iron oxide or hydroxide, and T between 1200º e 1565º C. O presente artigo trata da caracterização da composição mineralógica de azulejos antigos pertencentes aos séculos XVI, XVII e XIX, coletados em Salvador e Belém, visando à identificação da sua provável matéria-prima e a possível temperatura de queima. Quartzo foi identificado em todas as amostras. As demais fases cristalinas encontradas foram: mullita, cristobalita, calcita, anortita, hematita, gehlenita, diopsídio e wollastonita. Foi possível dividir as amostras em três grupos, em função da possível matéria-prima e temperatura de queima: grupo 1 - caulinita e quartzo, T entre 1200º e 1728º C; grupo 2 - quartzo, caulinita, calcita e/ou dolomita e óxido ou hidróxido de ferro, T entre 900º e 1200ºC; grupo 3 - quartzo, argilominerais (provavelmente caulinita), calcita e/ou dolomita e hidróxido ou óxido de ferro, T entre 1200º e 1565º C.