Silica gel with similar properties to commercial silica was obtained from blast furnace slag (EAF) using digestion with hydrochloric acid. The EAF-silica was obtained and characterized by different techniques. The results showed that the EAF-silica obtained was amorphous, with 99.7% purity and specific area 282 m2/g. It presented high hydrophilic character (12.27%), with constitution water of ~ 6.18%, which was confirmed by mass loss in thermogravimetric analysis. The EAF-silica particles had micrometric sizes (< 1 µm) with aggregates, unimodal size distribution and D50 7.0 µm.Sílica gel com propriedades similares à sílica comercial foi obtida a partir de escória de alto forno (EAF), utilizando digestão com ácido clorídrico. A EAF-sílica obtida foi caracterizada por diferentes técnicas, mostrando-se amorfa, com pureza 99,7% e área específica 282 m2/g. Apresentou caráter hidrofílico alto (12,27%), com água de constituição de ~ 6,18%, o que foi confirmado pela perda de massa durante a análise termogravimétrica. As partículas de EAF-sílica apresentaram tamanhos micrométricos (< 1 µm) em forma de agregados, distribuição granulométrica unimodal e D50 7,0 µm.