Influence of chloride ions concentration on the development of severe localised corrosion and its effects on the electrochemical response of the 2198-T8 alloy

dc.creatorMACHADO, CARULINE de S.C.
dc.creatorSILVA, REJANE M.P. da
dc.creatorARAUJO, JOAO V. de S.
dc.creatorMILAGRE, MARIANA X.
dc.creatorDONATUS, UYIME
dc.creatorVIVEIROS, BARBARA V.G. de
dc.creatorKLUMPP, RAFAEL E.
dc.creatorCOSTA, ISOLDA
dc.date2021
dc.date2022-03-17T13:23:47Z
dc.date2022-03-17T13:23:47Z
dc.date.accessioned2023-09-28T14:21:25Z
dc.date.available2023-09-28T14:21:25Z
dc.identifier1478-422X
dc.identifierhttp://repositorio.ipen.br/handle/123456789/32809
dc.identifier4
dc.identifier56
dc.identifier10.1080/1478422X.2020.1862390
dc.identifier0000-0002-4987-3334
dc.identifier37.64
dc.identifier47.33
dc.identifier.urihttps://repositorioslatinoamericanos.uchile.cl/handle/2250/9003028
dc.descriptionThe development of severe localised corrosion (SLC) on the 2198-T8 alloy was investigated in solutions of various NaCl concentrations (0.001, 0.005 and 0.01 mol L???1). Immersion tests, optical profilometry, conventional and local electrochemical analyses were performed to evaluate the corrosion behaviour of the alloy. Immersion tests showed that the alloy is susceptible to SLC in all conditions, although the pits sizes were dependent on the solution concentration. The largest anodic areas, corresponding to SLC sites, were observed for the sample immersed in 0.001 mol L???1 NaCl, whereas pits with similar sizes were observed for the samples immersed in solutions with 0.005 and 0.01 mol L???1 of NaCl. Moreover, the maximum depth of attack was observed for the sample immersed in 0.001 mol L???1 NaCl. These results were in agreement with the scanning ionselective electrode technique (SIET) maps which showed stronger acidification on the sample exposed to 0.001 mol L???1 NaCl solution.
dc.descriptionCoordena????o de Aperfei??oamento de Pessoal de N??vel Superior (CAPES)
dc.descriptionFunda????o de Amparo ?? Pesquisa do Estado de S??o Paulo (FAPESP)
dc.descriptionCAPES: 806-14; 88882.333459/2019-01; 88882.333479/2019-01
dc.descriptionFAPESP: 13/13235-6; 18/06880-6; 17/03095-3
dc.format341-350
dc.relationCorrosion Engineering, Science and Technology
dc.rightsclosedAccess
dc.subjectaluminium alloys
dc.subjectlithium alloys
dc.subjectcopper alloys
dc.subjectchlorides
dc.subjections
dc.subjectcorrosion
dc.titleInfluence of chloride ions concentration on the development of severe localised corrosion and its effects on the electrochemical response of the 2198-T8 alloy
dc.typeArtigo de peri??dico
dc.coverageI


Este ítem pertenece a la siguiente institución