An in situ high-temperature X-ray diffraction study of phase transformations in maraging 300 steel
Registro en:
0000-0003-1503-1582
Autor
REIS, A.G.
REIS, D.A.P.
ABDALLA, A.J.
OTUBO, J.
COUTO, A.A.
INTERNATIONAL CONFERENCE ON DIFFUSION IN SOLIDS AND LIQUIDS, 12th
Resumen
The phase transitions in the maraging 300 steel were studied using high temperature X-ray diffractometry.
Maraging are ultra-high resistant steels with Ni-Co-Mo-Ti presenting a broad range of application in key
areas such as nuclear and aerospace industries [1]. Prolonged high temperature exposure would lead to
the formation of equilibrium austenite and ferrite phases [2]. Solution annealed maraging 300 steel was
continuously heated at a 10 ??C/min rate from ambient temperature until 900 ??C and X-Ray measurements
were done at 25, 400, 500, 600, 650, 700, 800 and 900 ??C. Dilatometric curve at the same heating rate and
temperature range were performed and the results were compared with high temperature X-Ray diffraction.
The martensite to austenite transformation and vice-versa could be detected by both techniques, although
the precipitation could be detected only by dilatometry, associated to low volume of precipitates to be
detected by X-Ray diffraction. The effect of austenite reversion at 600??C was also studied after at 1, 2, 3
and 4 hour of exposure, showing that the amount of reverted austenite is proportional of time exposure at
high temperature.