Transmission electron microscopy characterization of protective La0.7Sr0.3MnO3???delta coatings prepared by electrostatic spray deposition on ferritic alloy
Registro en:
1793-6047
3
10
10.1142/S1793604717500126
19.123
Autor
CONCEICAO, LEANDRO da
LAY, SABINE
ROBAUT, FLORENCE
RENOU, GILLES
MUCCILLO, E.N.S.
DJURADO, ELISABETH
Resumen
The effect of La0:7Sr0:3MnO3 ?? (LSM) coating on SS446 steel on air oxidation at 800???C was investigated by transmission electron
microscopy. Dense and crack free thin LSM films were prepared by electrostatic spray deposition. The microstructural characterization
was carried out on coated and uncoated interconnectors. A thin chromia scale at the alloy interface along with two spinel
phases were observed after long term oxidation in both cases. Specimens exhibit, in addition, an SiO2 layer at the interface with
steel due to the high content of Si in the steel. Significant changes in the thickness, morphology and composition occurred in the
reaction layer for the LSM coated steel. These effects are explained on the basis of changes in the diffusive fluxes during exposure
to the oxidation treatment. The implications of these effects for the degradation mechanism of LSM-based interconnects are
discussed. Funda????o de Amparo ?? Pesquisa do Estado de S??o Paulo (FAPESP) FAPESP: 13/07296-2; 12/07648-3