The phase transitions that occur in the Cu-22.26 at.%Al-9.93 at.%Mn and Cu-22.49 at.%Al-10.01 at.%Mn-1.53 at.%Ag alloys after slow cooling were studied using differential scanning calorimetry at different heating rates, microhardness changes with temperature, magnetization changes with temperature, scanning electron microscopy and energy dispersion X-ray spectroscopy. The results indicated that the presence of Ag does not modify the transition sequence of Cu-Al-Mn alloy, introduces a new transition due to the (Ag-Cu)-rich precipitates dissolution at about 800 K, and changes the mechanism of DO 3 phase dissolution. This mechanistic change was analyzed and a sequence of phase transitions was proposed for the reaction. © 2013 Elsevier B.V.