Chestnut fruit shell and ground coffee waste were evaluated as filler raw materials for plywood adhesive. A phenol-formaldehyde (PF) resin was formulated in the laboratory for plywood manufacture. Specification characteristics were determined on the PF resin, including nonvolatile solids, gel time, viscosity, etc. The laboratory synthesized PF resin was mixed with extender, filler and NaOH. Plywoods were uniformly made with the PF resin mixture and tested for tension shear strength after aging method, modulus of rupture (MOR) and thickness swell according to the procedures of the Korean Standard KS F 3101 and KS F 3114. All plywood made with each filler type showed good physical and mechanical strength properties. The performance test results indicated that the chestnut fruit shell and ground coffee waste would be suitable as filler for plywood adhesive.A casca da castanha e resíduos de café moído foram avaliados como material de enchimento para produção de adesivo para compensados. Uma resina de fenol-formaldeído (FF) foi formulada em laboratório para fabricação de compensados. As propriedades da resina FF foram sólidos não voláteis, tempo de gelatinização (gel time),viscosidade, etc. A resina FF sintetizada em laboratório foi misturada com extensor, carga e NaOH. Os compensados foram feitos de maneira uniforme com a mistura de resina FF e testados quanto à resistência ao cisalhamento, módulo de ruptura (MOR) e inchamento em espessura, de acordo com as normas coreanas KS F 3101 e KS F 3114. Todos os compensados fabricados com cada tipo de carga apresentaram boas propriedades de resistência física e mecânica. Os resultados dos testes de desempenho indicaram que a casca da castanha e os resíduos de café moído são adequados como carga para produção de adesivo para fabricação de compensados.