The bending properties of a Eucalyptus saligna Smith clone were studied. Thirty trees, with age of approximately ten years, coming from Klabin-Riocell forests were used in the tests. The specimens, manufactured following ASTM D143-94 (1995), were tested in two series: after conditioning in standard room (200C and 65% relative humidity) or after water soaking. The results indicated values 1,296 and 1,4 times larger for air-dried when compared to moist wood, for bending stiffness and strength, respectively. Wood density, modulus of rupture and elasticity increased with fertilization and tree spacing.Neste trabalho, foram investigadas as propriedades de flexão estática da madeira de um clone de Eucalyptus saligna Smith. A madeira foi retirada da primeira tora de árvores procedentes de unidades experimentais da Klabin-Riocell com idade de, aproximadamente, 10 anos. As unidades foram estabelecidas com três diferentes espaçamentos (3 x 2, 3 x 3 e 3 x 4 m) e duas doses de adubação (400 ou 800 kg/ha). Trinta árvores (cinco por parcela) foram utilizadas nos ensaios. Os corpos de prova, confeccionados segundo a ASTM D143-93 (1995), foram testados após condicionados em câmara climatizada a 200C e 65% de umidade relativa ou após armazenamento em água. Os resultados indicaram valores 1,296 e 1,4 vezes maiores da madeira seca em relação à verde, para o módulo de elasticidade (MOE) e módulo de ruptura (MOR) respectivamente. Houve aumento da massa específica (ME), do MOR e do MOE com o espaçamento e com a adubação.