Solvothermal method to obtain europium-doped yttrium oxide
Registro en:
Journal of Solid State Chemistry. San Diego: Academic Press Inc. Elsevier B.V., v. 171, n. 1-2, p. 268-272, 2003.
0022-4596
10.1016/S0022-4596(02)00174-3
WOS:000183207400042
Autor
Davolos, Marian Rosaly
Feliciano, S.
Pires, Ana Maria
Marques, RFC
Jafelicci, M.
Resumen
Pure yttrium oxide or mixed with europium oxide (3 at%) were treated in supercritical isopropanolic suspension at 500degreesC for 20 It and filling degree of 50%. Products were supercritically dried and characterized by scanning electron microscopy (SEM), X-ray powder diffraction (XRD), infrared spectroscopy (IR) and luminescence spectroscopy (LS). Particle shape is irregular with an equivalent diameter of ca. 5 mum. Cubic crystalline phase is mainly obtained and hydroxide ion in low concentration is detected by IR vibrational spectrum. Europium in this concentration does not extensively change such observed characteristics from the pure yttrium oxide. Luminescence spectra show that the doped product is a mixture of the two oxides added by oxyhydroxide impurities. Nevertheless, this precursor sample, after being heated at 900degreesC during 1 h, has all characteristics, especially luminescent ones, of the P22 commercial phosphor. (C) 2003 Elsevier B.V. (USA). All rights reserved.