Effect of different light sources on degree of conversion, hardness and plasticization of a composite
Registro en:
journal of research in dentistry tubarão, v. 1, n. 2, p. 135-139, 2013.
2317-5907
4629404319391359
2201243962159442
4301268775018864
Autor
Barreto, Bruno de Castro Ferreira
Catelan, Anderson
Okida, Ricardo Coelho [UNESP]
Gonçalves, Gisele Fernanda [UNESP]
Silva, Gisele Rodrigues
Santos, Paulo Henrique [UNESP]
Xavier, Tathy Aparecida
Aguiar, Flávio Henrique Baggio
Soares, Carlos José
Resumen
Clinical performance of composite resins depends largely on their mechanical properties,and those are influenced by several factors,such as the light-curing mode. The purpose of this study was to evaluate the influence of different light sources on degree of conversion(DC), Knoop hardness(KHN) and plasticization(P) of a composite resin. Disc-shaped specimens (5 x 2 mm) of Esthet-X(Dentsply) methacrylate-based microhybrid composite were light-cured using quartz-tungsten-halogen (QTH) Optilight Plus(Gnatus) or light-emitting diode(LED) Ultraled(Dabi Atlante) curing units at 400 and 340 mW/cm2 of irradiance, respectively. After 24 h, absorption spectra of composite were obtained using Nexus 670(Nicolet)FT-IR spectrometer in order to calculate the DC.The KHN was measured in the HMV-2000(Shimadzu) microhardness tester under 50 g loads for 15 s, and P was evaluated by percentage reductio of hardness after 24 h of alcohol storage. Data were subjected to t-Student test(alpha=0.05).QTH device showed lower P and higher KHN$ than LED (p<0.05), and no difference between the light-curing units was found for DC (p>0.05). The halogen-curing unit with higher irradiance promoted higher KHN and lower softening in alcohol than LED. Department of Operative Dentistry and Dental Materials, Dental School, University of Uberlandia, Uberlandia, MG, Brazil Department of Restorative Dentistry, Piracicaba Dental School, University of Campinas, Piracicaba, SP, Brazil Department of Restorative Dentistry, Araçatuba School of Dentistry, State University of São Paulo (UNESP), Araçatuba, SP, Brazil Department of Dental Materials and Prostodontics, Araçatuba School of Dentistry, State University of São Paulo (UNESP), Araçatuba, SP, Brasil Department of Restorative Dentistry, Araçatuba School of Dentistry, State University of São Paulo (UNESP), Araçatuba, SP, Brazil Department of Dental Materials and Prostodontics, Araçatuba School of Dentistry, State University of São Paulo (UNESP), Araçatuba, SP, Brasil