Cementos óseos acrílicos modificados con 2 - dietilaminoetil acrilato e hidroxiapatita para aplicación como cementante de prótesis articulares
Autor
Suárez Berdugo, Kimberly
Institución
Resumen
In this work, the effect of the incorporation of hydroxyapatite and comonomer containing amine groups on the mechanical, thermical, morphological and chemical properties of acrylic bone cements was studied. Cements was prepared with 2-diethyl amino ethyl acrylate (DEAEA) as comonomer in the liquid phase. It was found that strength and modulus decreased with increasing comonomer content in bending and compressive tests. It was also observed the same behavior wih the peak temperatura and setting time. Strength compressive was also evaluated after soaking the specimens in Simulated Body Fluid (SBF) for one month. It was found that strength increase 1 Mpa when the samples were stored in SBF. En este trabajo se estudió el efecto de la incorporación de Hidroxiapatia y un co-monómero del grupo amino en las propiedades mecánicas, térmicas, morfológicas y químicas de cementos óseos acrílicos. Los cementos fueron preparados con 2-dietilaminoetil acrilato como co-monomero en la fase liquida. Se encontró que la resistencia y el módulo a compresión y flexión decrecen con el incremento del contenido de co-monomero. También se observó el mismo comportamiento con la temperatura máxima y el tiempo de curado. Se evaluó la resistencia a la compresión después de sumergir las probetas en Fluido Corporal Simulado (FCS) durante un mes. Se encontró que la resistencia aumento 1 MPa cuando las muestras se sumergieron en FCS. Universidad de San Buenaventura - Cali