Thermal characterization of the interaction of poly(3-hydroxybutyrate) with maleic anhydride
Registro en:
Journal of Thermal Analysis and Calorimetry. Dordrecht: Springer, v. 106, n. 2, p. 453-458, 2011.
1388-6150
10.1007/s10973-011-1706-3
WOS:000296065100023
0000-0002-7984-5908
Autor
Souza, J. L.
Santos, A. F.
Crespi, Marisa Spirandeli
Ribeiro, Clovis Augusto
Resumen
Poly(3-hydroxybutyrate), PHB, has been structurally modified with maleic anhydride, MA, in the presence of triethylamine, TEA. Glass transition, melting, and crystallization temperature, obtained from DSC curves, and thermal degradation temperatures obtained from TG ones, were employed to evaluate the influence of the MA proportion on the modification in the PHB chain. According to the results, most of chain modification reactions are the 80/20 and 90/10 proportions. Observations suggest that most chain modification reactions occur when the ratio of PHB/MA is 80/20 or 90/10. This suggests that modifications of PHB in the presence of MA involve main chain scission.