Compositional Design of Dielectric, Ferroelectric and Piezoelectric Properties of (K, Na)NbO3 and (Ba, Na)(Ti, Nb)O-3 Based Ceramics Prepared by Different Sintering Routes

Abstract

Lead free piezoelectric materials are being intensively investigated in order to substitute lead based ones, commonly used in many different applications. Among the most promising lead-free materials are those with modified NaNbO3, such as (K, Na)NbO3 (KNN) and (Ba, Na)(Ti, Nb)O-3 (BTNN) families. From a ceramic processing point of view, high density single phase KNN and BTNN ceramics are very difficult to sinter due to the volatility of the alkaline elements, the narrow sintering temperature range and the anomalous grain growth. In this work, Spark Plasma Sintering (SPS) and high-energy ball milling (HEBM), following heat treatments (calcining and sintering), in oxidative (O-2) atmosphere have been used to prepare single phase highly densified KNN (pure and Cu2+ or Li1+ doped), with theoretical densities (th) > 97% and BTNN ceramics ((th) similar to 90%), respectively. Using BTTN ceramics with a P4mm perovskite-like structure, we showed that by increasing the NaNbO3 content, the ferroelectric properties change from having a relaxor effect to an almost normal ferroelectric character, while the tetragonality and grain size increase and the shear piezoelectric coefficients (k(15), g(15) and d(15)) improve. For KNN ceramics, the results reveal that the values for remanent polarization as well as for most of the coercive field are quite similar among all compositions. These facts evidenced that Cu2+ may be incorporated into the A and/or B sites of the perovskite structure, having both hardening and softening effects.