Caracterização mecânica e microestrutural de um aço baixo carbono microligado com estrutura multifásica

dc.contributorUniversidade Estadual Paulista (UNESP)
dc.creatorEilises, C. C. A.
dc.creatorHashimoto, Tomaz Manabu
dc.creatorAbdalla, A. J.
dc.creatorPereira, Marcelo dos Santos
dc.date2014-05-20T13:28:10Z
dc.date2014-05-20T13:28:10Z
dc.date2008-06-01
dc.date.accessioned2017-04-05T20:10:40Z
dc.date.available2017-04-05T20:10:40Z
dc.identifierMatéria (Rio de Janeiro). Rede Latino-Americana de Materiais, v. 13, n. 2, p. 398-404, 2008.
dc.identifier1517-7076
dc.identifierhttp://hdl.handle.net/11449/9355
dc.identifier10.1590/S1517-70762008000200019
dc.identifierS1517-70762008000200019
dc.identifierWOS:000269834900019
dc.identifierS1517-70762008000200019.pdf
dc.identifierhttp://dx.doi.org/10.1590/S1517-70762008000200019
dc.identifier.urihttp://repositorioslatinoamericanos.uchile.cl/handle/2250/857528
dc.descriptionNeste trabalho foi realizada a caracterização mecânica e microestrutural de um aço microligado com estrutura multifásica. Foi aplicado tratamento térmico pré-determinado, objetivando a formação de uma microestrutura multifásica no material. Na caracterização microestrutural foram utilizados ataques químicos à base de metabissulfito de sódio e ácido pícrico, enquanto a caracterização mecânica foi realizada através de ensaios de tração. Os resultados demonstram o elevado potencial dos aços multifásicos em aplicações que necessitem de valores superiores de resistência e ductilidade, pois tanto para temperatura isotérmica de 400ºC quanto para 350ºC houve um ganho no limite de resistência à tração ficando em torno de 786MPa e 773MPa respectivamente, representando um aumento de 15,5% e 13,6% com relação ao material fornecido.
dc.descriptionA mechanical and microstructural characterization of a multiphase micro alloyed steel was realized in this work. A predetermined heat treatment was realized in order to nucleate a multiphase microstructure in the material. In the microstuctural characterization sodium metabisulfite and picric acid echants were applied, while the mechanical characterization was realized by tensile tests. The results showed a high potential of multiphase steel in applications that needs greater values of strength and ductility, because for both isothermal temperature of 400 º C to 350 º C as there was a gain in the limit of tensile strength getting around 786MPa and 773MPa respectively, representing an increase of 15.5% and 13.6% with respect to material provided.
dc.languagepor
dc.publisherRede Latino-Americana de Materiais
dc.relationMatéria (Rio de Janeiro)
dc.rightsinfo:eu-repo/semantics/openAccess
dc.subjectReagente Le Pera
dc.subjectaços multifásicos
dc.subjectcaracterização mecânica
dc.subjectcaracterização microestrutural
dc.subjectLe Pera etchant
dc.subjectmultiphase steels
dc.subjectmechanical characterization
dc.subjectmicrostructural characterization
dc.titleCaracterização mecânica e microestrutural de um aço baixo carbono microligado com estrutura multifásica
dc.typeOtro


Este ítem pertenece a la siguiente institución