| dc.contributor | Llano Mart?nez, Jorge Fredy | |
| dc.creator | Tapicha Urrea, Nicol?s | |
| dc.date | 2019-07-12T19:26:34Z | |
| dc.date | 2019-07-12T19:26:34Z | |
| dc.date | 2019 | |
| dc.date.accessioned | 2023-08-31T19:05:33Z | |
| dc.date.available | 2023-08-31T19:05:33Z | |
| dc.identifier | Tapicha Urrea, N. (2019). Evaluaci?n de la resistencia al desgaste adhesivo del acero AISI 1020 cementado con carb?n obtenido a partir de la c?scara de papa. [Tesis de pregrado, Universidad de Ibagu?]. http://repositorio.unibague.edu.co:80/jspui/handle/20.500.12313/1283 | |
| dc.identifier | http://repositorio.unibague.edu.co:80/jspui/handle/20.500.12313/1283 | |
| dc.identifier.uri | https://repositorioslatinoamericanos.uchile.cl/handle/2250/8555391 | |
| dc.description | En este trabajo se llev? a cabo la cementaci?n en el acero AISI 1020 (en cinco discos de 76 mm de di?metro y 8 mm de espesor) a 950 ?C con un tiempo de sostenimiento de 10 horas utilizando carb?n obtenido de la c?scara de papa. Se encontr? que utilizar este tipo de biomasa como agente cementante ayuda a mejorar propiedades en el acero como la dureza y resistencia al desgaste. En los resultados obtenidos se hizo evidente que el carb?n de c?scara de papa eleva el nivel de contenido de carbono en la superficie de los discos, logr?ndose obtener una profundidad de capa de 1013.23 ?m con un aumento en la dureza de 184 a 335 HV y una disminuci?n en el promedio de p?rdida de masa de 0.0470 a 0.0201 g. Se realizaron post-tratamientos de temple en agua, temple en aceite 10W30 y revenidos con el fin de observar el cambio microestructural y la influencia que tendr?an en la dureza y resistencia al desgaste del acero. De igual manera se obtuvo que el cementar, templar en aceite a 850 ?C y revenir a 400 ?C durante 80 minutos da las mejores condiciones de desgaste, reduci?ndose el promedio de p?rdida de masa hasta 0.0104 g. | |
| dc.description | In this work, cementation was carried out on AISI 1020 steel (on five discs 76 mm in diameter and 8 mm thick) at 950 ?C with a holding time of 10 hours using charcoal obtained from the potato peel. It was found that using this type of biomass as a cementitious agent helps to improve steel properties such as hardness and wear resistance. In the results obtained, it became evident that potato peel carbon raises the level of carbon content in the surface of the discs, obtaining a layer depth of 1013.23 ?m with an increase in hardness from 184 to 335 HV and a decrease in the average loss of mass from 0.0470 to 0.0201 g. Water quenching, 10W30 oil quenching and tempering post-treatments were performed in order to observe the microstructural change and the influence they would have on the hardness and wear resistance of the steel. It was also obtained that cementing, tempering in oil at 850 ?C and tempering at 400 ?C during 80 minutes gives the best conditions of wear, reducing the average loss of mass to 0.0104 g. | |
| dc.format | Application/pdf | |
| dc.format | application/pdf | |
| dc.format | application/pdf | |
| dc.language | es | |
| dc.publisher | Universidad de Ibagu? | |
| dc.publisher | Facultad de Ingenier?a | |
| dc.rights | Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License | |
| dc.rights | Manifiesto(amos) que el documento objeto de esta autorizaci?n es de mi(nuestra) exclusiva autor?a, tengo(emos) la titularidad plena sobre ?l y el mismo fue elaborado sin quebrantar ni suplantar los derechos de autor de terceros. En caso de queja o acci?n por parte de un tercero referente a los derechos de autor sobre el mismo, asumir?(mos) la responsabilidad total, y saldr?(mos) en defensa de los derechos aqu? autorizados a la Universidad de Ibagu?; por tanto, para todos los efectos, la Universidad de Ibagu? act?a como un tercero de buena fe.
Esta autorizaci?n no implica renunciar al derecho que tengo(emos) de publicar total o parcialmente el documento. Toda persona que consulte el documento, ya sea en la biblioteca o el medio electr?nico en donde sea reproducido, podr? copiar apartes del texto, siempre y cuando cite la fuente, es decir el t?tulo del documento y a m?(nosotros) como su(s) autor(es). | |
| dc.rights | https://creativecommons.org/licenses/by-nc-nd/4.0/ | |
| dc.subject | Cementaci?n s?lida | |
| dc.subject | Acero AISI 1020 | |
| dc.subject | C?scara de papa | |
| dc.subject | Dureza | |
| dc.subject | P?rdida de masa | |
| dc.subject | Ensayo de desgaste | |
| dc.subject | Solid cementation | |
| dc.subject | Steel AISI 1020 | |
| dc.subject | Potato peel | |
| dc.subject | Hardness | |
| dc.subject | Loss of mass | |
| dc.subject | Wear test | |
| dc.title | Asistencia de investigaci?n: Evaluaci?n de la resistencia al desgaste adhesivo del acero AISI 1020 cementado con carb?n obtenido a partir de la c?scara de papa | |
| dc.type | Bachelor Thesis | |
| dc.type | Tesis de pregrado | |