In this work we have synthesized silver nanoparticles in Poly (methyl methacrylate) (PMMA). This was achieved y polymerizing the mixture of monomer and corresponding metal compound, followed by post-heating treatment. The linear absorption coefficient of the samples was measured using a spectrophotometer, where an absorption peak at 420nm was observed. This peak grows up and shifts as a function of the concentration of the radical initiator. The linear refractive index was measured using the Fresnel equations and agrees with previous reported results. The nonlinear properties were obtained using the single lens Z-scan method, where the nonlinear absorption coefficient (Δα) was found between 5.5975514 and 17.9483493cm⁻¹. The nonlinear refractive index coefficient (Δη) was found to be negative and its value oscillates between 12.9099 E-06 and 22.4276 E-06. Finally, the third-order coefficient (χ³) was calculated in the range of 233–787 E-9 esu.