Novel Al-matrix nanocomposites reinforced with multi-walled carbon nanotubes

dc.creatorRAUL PEREZ BUSTAMANTE
dc.creatorIVANOVICH ESTRADA GUEL
dc.creatorWILBER ANTUNEZ FLORES
dc.creatorMARIO MIKI YOSHIDA
dc.date2008
dc.date.accessioned2023-07-21T15:31:47Z
dc.date.available2023-07-21T15:31:47Z
dc.identifierhttp://cimav.repositorioinstitucional.mx/jspui/handle/1004/2231
dc.identifier.urihttps://repositorioslatinoamericanos.uchile.cl/handle/2250/7728136
dc.descriptionNovel Al-based nanocomposites reinforced with multi-walled carbon nanotubes were produced by mechanical milling followed by pressure-less sintering at 823Kunder vacuum. The interface between Al matrix and the multi-walled carbon nanotubeswas examined using transmission electron microscopy. These observation showed that the multi-walled carbon nanotubes were not damaged during the preparation of the nanocomposite and that no reaction products were detected after sintering. The mechanical properties of sintered nanocomposites specimens were evaluated by a compression test. The yield stress (σy) and the maximum strength (σmax) obtained were considerably higher than those reported in the literature for pure Al prepared by the same route. The values for σy and σmax increase as the volume fraction of multi-walled carbon nanotubes increases. The milling time and the concentration of multi-walled carbon nanotubes have an important effect on the mechanical properties of the nanocomposite.
dc.formatapplication/pdf
dc.languageeng
dc.rightsinfo:eu-repo/semantics/openAccess
dc.rightshttp://creativecommons.org/about/cc0/
dc.subjectinfo:eu-repo/classification/ELECTRON MICROSCOPY/NANOSTRUCTURES
dc.subjectinfo:eu-repo/classification/cti/2
dc.subjectinfo:eu-repo/classification/cti/23
dc.subjectinfo:eu-repo/classification/cti/2399
dc.subjectinfo:eu-repo/classification/cti/239999
dc.subjectinfo:eu-repo/classification/cti/239999
dc.titleNovel Al-matrix nanocomposites reinforced with multi-walled carbon nanotubes