Protection against the hot corrosion of carbon steel by thermal spraying
Protección contra la corrosión por sales fundidas de un acero al carbono por rociado térmico
| dc.creator | Marulanda Arévalo, José Luddey | |
| dc.creator | Gamboa, David | |
| dc.creator | Posada, Brayan André | |
| dc.date | 2011-03-07T20:43:11Z | |
| dc.date | 2021-11-02T19:31:12Z | |
| dc.date | 2011-03-07T20:43:11Z | |
| dc.date | 2021-11-02T19:31:12Z | |
| dc.date | 2007 | |
| dc.identifier | Scientia et Technica Año XIII No. 36 (Septiembre 2007) | |
| dc.identifier | 0122-1701 | |
| dc.identifier | http://www.utp.edu.co/php/revistas/ScientiaEtTechnica/docsFTP/12235086.pdf | |
| dc.identifier | https://hdl.handle.net/11059/216 | |
| dc.description | Se evaluó la corrosión por sales fundidas mediante técnicas gravimétricas en un acero al carbono rociado térmicamente con una aleación de acero inoxidable, en una mezcla de sal 20% Na2SO4 - 80% V2O5, entre temperatura de 500 ºC-650 ºC. Las pruebas gravimétricas mostraron una buena protección de la capa rociada térmicamente y la mayor degradación que sufrió el recubrimiento protector generalmente ocurrió a temperaturas superiores a las temperaturas de fusión de las sales, además la velocidad de corrosión aumenta con la temperatura y disminuye con el tiempo de exposición. | |
| dc.description | The hot corrosion was evaluated by gravimetric techniques of carbon steel protected by thermal spraying with a stainless alloy, in a mixture of salt 20% Na2SO4 - 80% V2O5, between temperature of 500 ºC - 650 ºC.. The gravimetric tests showed a good protection of the layer thermal spraying. The greater degradation than underwent the protective coating happened generally to temperatures superior to the temperatures of fusion of the salts, in addition the corrosion rate increases with the temperature and diminishes with time of exposure. | |
| dc.format | ||
| dc.format | application/pdf | |
| dc.format | application/pdf | |
| dc.language | spa | |
| dc.publisher | Pereira : Universidad Tecnológica de Pereira | |
| dc.publisher | Facultad de Ciencias Básicas | |
| dc.rights | Attribution-NonCommercial-NoDerivatives 4.0 International | |
| dc.rights | Open Access | |
| dc.rights | http://creativecommons.org/licenses/by-nc-nd/4.0/ | |
| dc.subject | Corrosión | |
| dc.subject | Sales fundidas | |
| dc.subject | Pentoxido de vanadio | |
| dc.subject | Perdida de peso | |
| dc.subject | Sulfato de sodio | |
| dc.subject | Mass loss | |
| dc.subject | Salts fused | |
| dc.subject | Sodium sulfate | |
| dc.subject | Vanadium pentoxide | |
| dc.title | Protection against the hot corrosion of carbon steel by thermal spraying | |
| dc.title | Protección contra la corrosión por sales fundidas de un acero al carbono por rociado térmico | |
| dc.type | Article |