dc.creatorPérez Fierro, Luis Manuel
dc.creatorRodríguez Gonzáles, Edgar Allan Max
dc.creatorTORRES HERNANDEZ, YARET GABRIELA; 310659
dc.creatorALTAMIRANO TORRES, ALEJANDRO; 44568
dc.creatorPérez Fierro, Luis Manuel
dc.creatorRodríguez Gonzáles, Edgar Allan Max
dc.creatorTorres Hernández, Yaret Gabriela
dc.creatorAltamirano Torres, Alejandro
dc.date.accessioned2023-01-19T18:07:14Z
dc.date.accessioned2023-07-20T16:20:05Z
dc.date.available2023-01-19T18:07:14Z
dc.date.available2023-07-20T16:20:05Z
dc.date.created2023-01-19T18:07:14Z
dc.date.issued2021
dc.identifierhttp://hdl.handle.net/11191/9310
dc.identifier.urihttps://repositorioslatinoamericanos.uchile.cl/handle/2250/7718679
dc.description.abstractEn el presente estudio, se analiza la influencia de diferentes tiempos y temperaturas de bainitizado en la microestructura y comportamiento mecánico de un acero grado maquinaria (AISI 5160). Se determinaron las fases presentes después de realizado el tratamiento térmico, en las diferentes muestras mediante microscopía óptica, a fin de relacionarlas con sus propiedades mecánicas. Así mismo se realizaron ensayos de dureza e impacto, para poder determinar las condiciones óptimas de tratamiento térmico. En general las muestras presentan mezclas de fases de ferrita y perlita, en algunos casos se pudo observar bainita inferior en la microeestructura. El valor de dureza más alto perteneció a la temperatura de 315°C, misma que también presentó la mayor resistencia al impacto.
dc.description.abstractThis research study the influence of different times and temperatures of austempered in the microstructure and mechanical behavior of a steel grade machinery (AISI 5160). The phases present after the heat treatment were determined, in the different samples by optical microscopy, in order to relate them to the mechanical behavior. Hardness and impact tests were also carried out in order to determine the optimal heat treatment conditions. In general, the samples present mixtures of ferrite and pearlite phases, in some cases lower bainite could be observed in the microstructure. The highest hardness value belonged to the temperature of 315°C, which also presented the highest impact resistance.
dc.languagespa
dc.publisherUniversidad Autónoma Metropolitana (México). Unidad Azcapotzalco. División de Ciencias Básicas e Ingeniería.
dc.rightshttp://creativecommons.org/licenses/by-nc-nd/4.0
dc.rightsopenAccess
dc.rightsAtribución-NoComercial-SinDerivadas
dc.sourceRevista Tendencias en Docencia e Investigación en Química. Año 7, número 7 (enero-diciembre de 2021). ISSN: 2448-6663
dc.subjectBainitizado, tenacidad, Dureza. Austempering, toughness, hardness.
dc.titleInfluencia de la temperatura de bainitizado en la microestructura y comportamiento mecánico de un acero grado maquinaria