Analysis of color and hardness of a medical silicone with extrinsic pigmentation after accelerated aging
Fecha
2020-10-01Registro en:
European Journal of Dentistry, v. 14, n. 4, p. 634-638, 2020.
1305-7464
1305-7456
10.1055/s-0040-1715782
2-s2.0-85092576559
Autor
Universidade Estadual Paulista (UNESP)
Institución
Resumen
Objective The aim of this study is to evaluate the color alteration and shore A hardness of a medical silicone with extrinsic pigmentation, before and after accelerated aging. Materials and Methods Twenty samples (Silastic Q7-4735) were made with an intrinsic pigmentation. This intrinsic pigmentation was composed of a pink pigment (H-109-P, Factor II) and an opacifier (ZnO). All samples had standardized dimensions (45-mm diameter and 2-mm thickness). Half of the 20 samples manufactured subsequently received an extrinsic pigment (Tan FE-215, Factor II). Therefore, two groups were created (n = 10): Group 1, group with intrinsic pigmentation and without extrinsic pigmentation (control) and Group 2, group with intrinsic and extrinsic pigmentation. Samples were submitted to color and Shore A hardness tests, before and after 1,008 hours of aging. Statistical Analysis Color alteration data were submitted to Student's t -test (a = 0.05). Shore A hardness data were submitted to two-way analysis of variance and Tukey test (a = 0.05). Results The incorporation of the extrinsic pigment on the silicone did not affect its color (?E) when the two groups were compared (p = 0.232). Regarding the hardness test, the interaction between group and period did not interfere with the hardness results(p =0.599). However, the period factor showed that there was a reduction in the hardness of the silicone after aging (p < 0.05). Conclusion In this study, all the hardness and color results of the silicone used were clinically acceptable, regardless of the presence of extrinsic pigmentation.