In this work, MCM-41 mesoporous silicates were prepared and modified with transition metals (Fe, Co) by a direct synthesis method. The influence of the metal content was tested varying the initial molar Si/Metal ratio (120, 60 or 20). The different meso-structures obtained were characterized by XRD, UVVIS-RD, N2 adsorption and the magnetic behavior was studied at room temperature. All samples showed typical paramagnetic behavior, indicating high dispersion metal species. There was also an important superparamagnetic contribution for samples with the highest iron loading, indicating a greater magnetic interaction between the nano-species.En este trabajo se prepararon silicatos mesoporosos del tipo MCM-41 modificados con metales de transición (Fe, Co) mediante el método de síntesis directa. Se evaluó la influencia del contenido de metal variando la relación molar inicial de Si/Metal (120, 60 o 20). Las diferentes meso-estructuras obtenidas se caracterizaron mediante DRX, UVvis-RD, adsorción de N2 y se estudió su comportamiento magnético a temperatura ambiente. Todas las muestras mostraron un comportamiento típicamente paramagnético, lo que indica una alta dispersión de las especies metálicas. Se observó además una importante contribución superparamagnética para la carga mayor de Fe, indicando mayor interacción magnética entre las nano-especies.