In this work, the crushing strength of the hybrid wood Hybrid Pinus elliottii var. Elliottii x Pinus caribaea var. Hondurensis,coming from the Province of Misiones, Argentina, has been determined – a base parameter to establish the load capacity of a wood joints. 118 specimens of 24 mm of thickness and other dimensions adjusted to Norm, with rigid bolt of 7 mm of diameter have been tested, according to the UNE-EN 383 Norm, of which 74 specimens were tested in a direction parallel to the fiber and 44 in perpendicular direction. The values of characteristic resistance to the crushing obtained were of 22 N/mm2 and 15 N/mm2 for the parallel and perpendicular directions respectively. For the set of test specimens, the density was determined, a high correlation with the crushing tensions being found. Values for the expected deformations in different loading conditions have been calculated.  The results obtained were compared with the NDS values.En este trabajo se ha determinado la resistencia al aplastamiento de la madera del Híbrido Pinus elliottii var. elliottii x Pinus caribaea var. hondurensis procedente de la Provincia de Misiones, Argentina, parámetro base para establecer la capacidad de carga de una unión.Se han ensayado 118 probetas de 24 mm de espesor y demás dimensiones ajustadas a norma con perno rígido de 7 mm de diámetro de acuerdo a la Norma UNE-EN 383, de las cuales 74 probetas se ensayaron en dirección paralela a la fibra y 44 en dirección perpendicular. Los valores de resistencia característica al aplastamiento obtenidos fueron de 22 N/mm2 y de 15 N/mm2 para las direcciones paralela y perpendicular respectivamente. Para el conjunto de probetas se determinó la densidad, encontrándose una alta correlación con las tensiones de aplastamiento. Se han calculado valores para las deformaciones esperables en distintas condiciones de carga. Se comparan los resultados obtenidos con las NDS.