Efectos del Ingreso de Hidrógeno en Juntas de Acero Soldadas Mediante el Proceso SMAW en Acero de Contenido Medio de Carbono
Autor
Bertucelli, Mariano
Inés, Mariano
Marconi, Cesar
Mansilla, Graciela
Institución
Resumen
The heat generated by the welding arc breaks the hydrogen bonding (H) of the molecules of the surrounding atmosphere, releasing two hydrogen atoms per dissociation. The introduction thereof in the weld metal is mainly attributed to the absorption of these atoms entering into the metal net. In this paper, coupons of SMAW welds were performed using both dry and high-humidity electrodes. Also electrolytic hydrogen charging on tensile specimens constructed from welded joints with dry electrode were made to simulate aggressive conditions of H entry. El calor generado por el arco eléctrico de la soldadura rompe el enlace de hidrógeno (H) de las moléculas de la atmósfera circundante, liberando dos átomos de hidrógeno por cada disociación. La introducción de los mismos en el metal de soldadura es atribuida fundamentalmente a la absorción de estos átomos que ingresan en la red metálica. En este trabajo se realizaron cupones de soldaduras SMAW empleando electrodos tanto secos como con alto contenido de humedad. Además se efectuó carga electrolítica de hidrógeno sobre probetas de tracción construidas a partir de uniones soldadas con electrodo seco para simular condiciones agresivas de ingreso de H.