This paper theoretically and experimentally studied the relationship between density and mechanical properties of particleboards obtained from 88.5% of wood chips and 11.5% of urea-formaldehyde resin with 57.35% solids. Paricleboards of 550, 650 and 750 Kg/m3 nominal densities (A, B, and C; respectively) at temperature = 150 °C, pressure = 30 Kg/cm2 and time = 10 min. were obtained. Final properties such as density, bending and internal bond were measured. The density and the internal bond of the panels A and B were statistically equal. Also, a simple regression model that relates density with internal bond, bending strength and flexural modulus, respectively; was adopted.En este trabajo se estudió teórica y experimentalmente la relación entre la densidad y las propiedades mecánicas de paneles de madera conglomerada obtenidos a partir de un 88,5% de partículas de madera y un 11,5% de resina de urea-formaldehído con un 57,35% de sólidos. Se obtuvieron paneles de madera conglomerada de densidades nomimales de 550, 650 y 750 Kg/m3(A, B, y C; respectivamente) a temperatura = 150 ºC, presión = 30 Kg/cm2y tiempo = 10 min. Se midieron propiedades finales como densidad, flexión y adherencia interna. Tanto la densidad como la adherencia interna de los paneles A y B resultaron estadísticamente iguales. Además, se adoptó un modelo de regresión simple que correlaciona densidad con adherencia interna, resistencia en flexión y módulo de elasticidad en flexión, respectivamente.