In this work, it was studied the synthesis of bimodal mesoporous solids Ti-UVM-7, using the synthesis strategy known as the atrane way, with incorporation of Ti into synthesis gel in Si/Ti molar ratios of 10, 25, 50 and 100. The characterizations used were: X-ray diffraction, N2 adsorption-desorption isotherms, transmission electron microscopy and X-ray energy dispersive. For all solids, X-ray patterns showed peaks around 2.02 degrees of 2θ, isotherms were type IV, with two volume steps at relative pressures of 0.4 and 0.9, typical of UVM-7 materials, and BET surface areas of 1216 to 128 m2/g, decreasing as the content of Ti increased (decrease of the Si / Ti molar ratio). The amount of Ti incorporated was too similar to that initial placed in the synthesis gel, except for the solid with a Si/Ti molar ratio of 100 (initial), which only reached Si / Ti = 127.En este trabajo se estudió la síntesis de sólidos mesoporosos bimodales Ti-UVM-7, empleando la estrategia de síntesis conocida como la vía de los atranos, con la incorporación del Ti en el gel de síntesis en relaciones molares Si/Ti de 10, 25, 50 y 100. Las caracterizaciones empleadas fueron: difracción de rayos X, isotermas de adsorción-desorción de N2, microscopía electrónica de transmisión y energía dispersiva de rayos X. Para todos los sólidos, los patrones de DRX presentaron picos alrededor de 2,02 grados de 2θ, las isotermas fueron del tipo IV, con dos saltos de volumen a presiones relativas de 0,4 y 0,9 típico de los materiales UVM-7 y las áreas superficiales BET fueron de 1216 a 128 m2/g, disminuyendo en la medida que el contenido de Ti se fue incrementando (disminución de la relación Si/Ti). La cantidad de Ti incorporado fue muy similar a la inicial incorporada en el gel de síntesis, excepto para el sólido de relación molar de Si/Ti de 100 (inicial), que sólo llegó a Si/Ti=127.