Morfología de polvo de aluminio por estereología
Autor
Tolosa Chacón, Ramón Alexis
Ochoa, M.
Núñez, C.
Jáuregui Olazabal, Manuel
Institución
Resumen
The aluminum alloy powder particle form was quantitatively characterized by means the stereological method. With two-dimensional digitized images of the particles, the stereological parameters that qualify the form were determined through the use of computer programs. The results were statistically evaluated and represented in graphics for determine their behavior in dependence of particles’ size. In general the results agree with the fundament of sterology; the Bulkiness Factor parameter is the most representative of the form, while the Compactness Factor is very sensitive to the changes of particles size. Different parameters that determine a same peculiarity of the form present similar behavior. La forma de las partículas de un polvo de aleación de aluminio se caracterizó cuantitativamente mediante el método estereológico. Parámetros estereológicos que califican la forma se determinaron mediante programas de computación, a partir de imágenes bidimensionales digitalizadas de las partículas. Los resultados se evaluaron estadísticamente y se graficaron para determinar su comportamiento en dependencia de los tamaños de las partículas. En general los resultados concuerdan con los fundamentos de la estereología, el parámetro Factor de Volumen es el más representativo de la forma, mientras que el Factor de Compacticidad es muy sensible a los cambios del tamaño de las partículas. Parámetros diferentes que determinan una misma peculiaridad de la forma presentan comportamientos similares.